Microtensile bond strength of resin cements to 3-D printed and milled temporary restorative resins / Resistencia de unión en microtracción de cementos resinosos a resinas para provisionales impresas y fresadas

Abstract To evaluate the microtensile bond strength (µTBS) of two resin cements to 3D printed and milled CAD/CAM resins used for provisional fixed partial dentures. Blocks (5 x 5 x 5 mm) of three 3D-printed resins (Cosmos3DTemp / Yller; Resilab3D Temp / Wilcos and SmartPrint BioTemp, / MMTech) were printed (Photon, Anycubic Technology Co.). A milled material (VitaCAD-Temp, VITA) was used as control. Half the specimens were sandblasted and the rest were untreated. Two blocks were bonded with the corresponding resin cement: PanaviaV5 (Kuraray Noritake) and RelyX Ultimate (3M Oral Care). After 24 hours, the bonded blocks were sectioned into 1 x 1 mm side sticks. Half the beams were tested for µTBS and the other half was thermocycled (5000 cycles, 30s dwell-time, 5s transfer time) before µTBS testing. A four way Generalized Linear Model (material*sandblasting*cement*aging) analysis was applied. VITA exhibited the lowest µTBS, regardless of the cement, sandblasting and thermocycling. Sandblasting significantly improved the µTBS of VIT, especially after aging, but did not improve the µTBS of 3D printed resins. Sandblasting was not beneficial for 3D printed resins, although is crucial for adhesive cementation of milled temporary resins. Airborne particle abrasion affects the integrity of 3D-printed resins, without producing a benefit on the microtensile bond strength of these materials. However, sandblasting is crucial to achieve a high bond strength on milled temporary resins.

Resumen Evaluar la resistencia adhesiva en microtracción (µTBS) de dos cementos resinosos a resinas CAD/CAM impresas y fresadas indicadas para restauraciones provisionales. Bloques (5 x 5 x 5mm) de tres resinas impresas (Cosmos3DTemp / Yller; Resilab3D Temp / Wilcos and SmartPrint BioTemp, / MMTech) y una resina fresada (VitaCAD-Temp, VITA) fueron fabricados. La mitad de los especímenes fueron arenados y el resto no recibió tratamiento mecánico. Dos bloques con condiciones de tratamiento iguales fueron cementados con cemento resinoso (PanaviaV5 / Kuraray Noritake y RelyX Ultimate / 3M Oral Care). Después de 24 horas los bloques fueron seccionados en palitos de 1 mm² de área. En la mitad de los especímenes se midió la TBS inmediatamente y el resto fue termociclado (5000 ciclos, 30s remojo, 5s transferencia) antes de la prueba de TBS. Se aplica un análisis estadístico por Modelo Linear General con 4 factores (material*arenado*cemento*termociclado). La resina VITA presentó la menor µTBS, independientemente del cemento usado, el arenado y el termociclado. Sin embargo, el arenado aumentó la µTBS de VIT, especialmente después del termociclado. Por otro lado, el arenado no resultó en un aumento significativo de la µTBS de las resinas impresas. El arenado no fue beneficiosos para las resinas impresas, aunque es un paso crucial para la cementación adhesive de las resinas fresadas. El arenado afecta la integridad de las capas de las resinas impresas, sin generar un beneficio en la TBS.

Facetas diretas em resina composta utilizando o fluxo digital para planejamento: relato de caso / Direct facets in composite resin using digital flow for planning: case report / Facetas directas en resina compuesta utilizando flujo digital para planificación: reporte de caso

Introdução:O aprimoramento das resinas compostas nos últimosanos em associação com a difusão de informações nas redes sociais tornou as facetas diretas tratamentos populares na dentística restauradora. No entanto, são procedimentos que exigem ampla destreza manual e conhecimento técnico. O fluxo digital através doescaneamento, enceramento digital e prototipagem 3D para construção de guias tem se tornado uma excelente alternativa para aumentar a previsibilidade e aumentar a longevidade destes trabalhos. Objetivo:Descrever o protocolo de confecção de facetas diretas em resina composta, através de um relato de caso, utilizando como auxílio o planejamento digital para confecção de modelo 3D, guia de silicone e paredes palatinas. Descrição do Caso:Paciente do gênero masculino, 43 anos, queixava-se do formato dos seus dentes. Ao exame clínico percebeu-se desgaste dental nos incisivos centrais e linha do sorriso levemente invertida. Após duas sessões de clareamento de consultório com Peróxido de hidrogênio (35%) e mockup direto com resina composta, foi realizada a moldagem e escaneamento do modelo de gesso no laboratório. O enceramento digital foi aprovado, o modelo 3D foi impresso para confecção da guia de silicone. Com auxílio da guia foram executadas facetas diretas nos elementos 13, 12, 11, 21, 22 e 23. Conclusão:O fluxo digital pode ser uma alternativa viável para minimizar as falhas na confecção de facetas diretas em resina composta (AU).

Introduction:The improvement of composite resins in recent years, together with information disseminated on social media, has made direct veneers popular treatments in restorative dentistry. However, these procedures require significant manual dexterity and technical knowledge. Digital work flow using scanning, digital wax-up and 3D prototyping for the construction of guides has become an excellent alternative to increase predictability and the longevity of these procedures. Objective:Describe the manufacturing protocol for direct composite resin veneers, using a case report and digital to construct the 3D model, silicone guide and palatine walls. Case description:Male patient, 43 years old, complained of the shape of his teeth. Clinical examination revealed tooth wear on the central incisors and a slightly inverted smile line. After two whitening sessions with hydroigen peroxide (35%) and direct mockup with composite resin, the plaster model was molded and scanned in the laboratory. Digital wax-up was approved, and the 3D model was printed to manufacture the silicone guide. With the help of the guide, the direct veneers were applied to elements 13, 12, 11, 21, 22 and 23.Conclusions:Digital flow may be a feasible alternative to minimize manufacturing flaws in direct composite resin veneers (AU).

Introducción: La mejora de las resinas compuestas en los últimos años, y la difusión de información en las redes sociales, ha popularizado las facetas directas en los tratamientos en odontología restauradora. Sin embargo, son procedimientos que requieren demasiado destreza manual y conocimientos técnicos. El flujo digital usando escaneo, encerado digital y prototipado 3D para la construcción de guías se ha convertido en una excelente alternativa para aumentar la previsibilidad y la longevidad de estos procedimientos. Objetivo: Describir el protocolo para la realización de carillas directas en resina compuesta, a través de un reporte de caso, utilizando el planeo digital como ayuda para la realización de un modelo 3D, guía de silicona y paredes palatinas. Descripción del caso: Paciente masculino, 43 años, se quejó de la forma de sus dientes. El examen clínico reveló desgaste dental en los incisivos centrales y una línea de sonrisa levemente invertida. Después de dos sesiones de blanqueamiento en consultorio con peróxido de hidrógeno (35%) y maqueta directa con resina compuesta, el modelo de yeso fue moldeado y escaneado en el laboratorio. El encerado digital fue aprovado, el modelo 3D fue impreso para hacer la guía de silicona. Con la ayuda de la guía se realizaron carillas directas en los elementos 13, 12, 11, 21, 22 y 23. Conclusiones: El fluxo digital puede ser una alternativa viable para minimizar fallas en la fabricación de carillas directas en resina compuesta (AU).

Tecnologia digital em próteses totais: propriedades dos materiais CAD-CAM e desenvolvimento de uma patente de inovação para simplificação do fluxo de trabalho / Digital technology in complete dentures: properties of CAD-CAM materials and development of an innovation patent to simplify the workflow

Recursos digitais, como a manufatura subtrativa (fresagem CAD-CAM) e a manufatura aditiva (impressão 3D) podem promover significativos avanços, reduzindo o tempo e o custo de produção de próteses totais (PTs). Assim, este estudo objetiva investigar as características superficiais (rugosidade e ângulo de contato), propriedades mecânicas (resistência mini-flexural) e a adesão de biofilme sobre polímeros de PMMA pré-polimerizado para fresagem CAD-CAM e sobre resinas para impressão 3D utilizados na fabricação de bases de PTs, bem como propor um fluxo de trabalho inovador para abreviar e simplificar as etapas de confecção de PTs. Para a análise in vitro, foram fabricados um total de 60 discos e 40 barras distribuídas igualmente em quatro grupos: fresagem CAD-CAM (GF), impressão 3D (GI) e PMMA convencional termopolimerizado por ciclo longo (GCL) ou por energia de micro-ondas (GCM). A rugosidade foi determinada pelo valor de Ra; o ângulo de contato foi medido pelo método da gota séssil; o teste de resistência à mini-flexão foi obtido por teste de flexão de três pontos, enquanto o comportamento frente à formação de biofilme foi analisado através da adesão de biofilme de C. albicans. Os dados foram analisados por meio de estatística descritiva e analítica (α = 0,05). Os resultados mostraram que o GI apresentou a maior rugosidade superficial (Ra: 0,317 ± 0,151µm) e os menores valores de resistência à miniflexão (57,23 ± 9,07MPa) e o GF apresentou a menor adesão de biofilme de C. albicans (log UFC/mL: 3,74 ± 0,57) e maior média de resistência à mini-flexão (114,96 ± 16,23 MPa). Não houve diferença estatística entre o GF e os grupos convencionais para rugosidade, ângulo de contato e resistência à mini-flexão. A patente de inovação desenvolvida estabeleceu um novo fluxo de trabalho para confecção de próteses totais através de um protocolo de três consultas em que foram feitas as moldagens anatômicas na 1ª sessão, juntamente com o registro do suporte labial, plano oclusal e linhas de referência para subsidiar a montagem dos dentes superiores. Uma prótese-teste foi confeccionada por meio de procedimentos convencionais ou CAD-CAM e avaliada na 2ª consulta, permitindo observar o resultado estético, executar a moldagem funcional e realizar o registro da relação maxilo-mandibular, fornecendo referências precisas para a confecção da prótese inferior. Com base nos resultados da fase in vitro deste estudo, os corpos-de-prova obtidos a partir de disco para fresagem CAD-CAM apresentaram resistência flexural e propriedades superficiais semelhantes às resinas convencionais e mostraram um comportamento inibidor da adesão de C. albicans, enquanto os espécimes produzidos por impressão 3D exibiram a menor resistência à flexão e a maior rugosidade da superfície. O dispositivo inovador apresentado para a execução das etapas clínicas relacionadas à fabricação de PTs mostrou-se efetivo para abreviar e simplificar as técnicas disponíveis, apresentando confiabilidade e previsibilidade para produção de PTs em número de sessões reduzido (AU).

Digital features like subtractive and additive manufacturing can promote breakthroughs by reducing the time and cost of making complete dentures (CDs). Thus, this study aims to investigate surface characteristics (roughness and contact angle), mechanical properties (mini-flexural strength), and biofilm adhesion on computer-aided design/computer-aided manufacturing (CAD-CAM) PMMA polymer, and threedimensional (3D) printed resin for denture´s base fabrication as well as to propose an innovative workflow. For in vitro analysis, a total of 60 discs and 40 rectangular specimens were fabricated from one CAD-CAM pre-polymerized PMMA disc (GF), one 3D-printed (GI), and two conventional heat-polymerized (GCL and GCM) materials for denture base fabrication. Roughness was determined by the Ra value; the contact angle was measured by the sessile drop method; the mini-flexural strength test was a three-point bending test while the biofilm formation inhibition behavior was analyzed through C. albicans adhesion. The data were analyzed using descriptive and analytical statistics (α = 0.05). Results showed that GI specimens presented the highest surface roughness (Ra: 0.317 ± 0.151 µm) and lowest mini-flexural strength values (57.23 ± 9.07 MPa) and the GF showed the lowest C. albicans adhesion (log CFU/mL: 3.74 ± 0.57) and highest mini-flexural strength mean (114.96 ± 16.23 MPa). There was no statistical difference between GF and conventional groups for roughness, contact angle, and mini-flexural strength. In turn, the presented novel workflow for complete dentures fabrication reached a three appointments protocol in which preliminary impressions were made in the 1st session, all together to maxillary registration of lip support, occlusal plane, and reference lines for teeth arrangement. A trial denture was manufactured and evaluated by the 2nd appointment through conventional or CAD-CAM procedures, allowing esthetics evaluation, final impression, and maxillomandibular relationship record and providing precise references for final dentures fabrication. Based on the findings of this in vitro study, GF presented surface and mechanical properties similar to conventional resins and show improved behavior preventing C. albicans adhesion, while GI specimens exhibited the lowest flexural strength, and highest surface roughness. The proposed device for CD´s fabrication clinical procedures reached feasibility and by simplifying available techniques, this protocol could achieve reliability and predictability to produce complete dentures with reduced working time (AU).

Resinas acrílicas utilizadas em placas estabilizadoras: resistência a fraturas e ensaio microbiológico / Acrylic resins used in stabilizer plates: resistance to fractures and microbiological testing

O aprimoramento da tecnologia CAD/CAM permitiu a confecção de placas estabilizadoras digitais, no entanto, há lacunas acerca do comportamento desses dispositivos frente a variáveis mecânicas e biológicas ainda desconhecidas. Dessa forma, o objetivo desse trabalho foi verificar se as resinas utilizadas na tecnologia digital das placas fresadas e impressas são capazes de influenciar na resistência à fratura e na adesão de micro-organismos em detrimento das resinas empregadas na confecção das placas termopolimerizáveis convencionais e se as propriedades testadas se relacionam com a variação da espessura desses dispositivos. Para tanto, foi realizado um estudo in vitro que contou com as fases mecânica e microbiológica, sendo cada uma composta pelos grupos Convencional (GC) (n=30), Fresado (GF) (n=30) e Impresso (GI) (n=30), de acordo com o método de confecção, possuindo cada um três subgrupos (n=10) que variaram a espessura dos espécimes de 1 a 3 mm. Na fase mecânica, as amostras, com formato de barras de 65 mm, foram testadas quanto à resistência à fratura na máquina de ensaios universal, com célula de carga de 500 kgf e velocidade de 1 mm/min; na microbiológica, a forma foi de discos com 15 mm de diâmetro, submetidos à adesão de micro-organismos à superfície com a exposição a Streptococcus mutans e mantidos por 24h a 35 °C em estufa para sucessiva contagem de UFC, com controle positivo. Os testes foram feitos em triplicata e os dados foram armazenados no SPSS 22.0 e a análise estatística contou com a ANOVA e o pósteste de Tukey. Nos resultados da fase mecânica, o ANOVA identificou diferenças estatisticamente significativas entre os grupos (p≤0,005), mostrando que GC e GF apresentaram melhores resultados. O pós-teste de Tukey considerou diferença estatisticamente significativa entre GF e GI (p=0,031), elencando GF como superior. Para a fase microbiológica, não foram verificadas diferenças estatísticas entre os grupos (p>0,005) em nenhuma das análises. Observou-se que para a resistência a fraturas, as resinas do modo fresado descreveram resultados superiores e/ou próximos aos da técnica convencional; e que as resinas da técnica digital e convencional, quanto à adesão superficial de micro-organismos, não diferiram entre si (AU).

CAD/CAM technology allowed the stabilizing splints manufacture, however there are gaps about these devices' behavior in face of mechanical and biological variables that are still unknown. Thus, the objective of this project was to verify if the resins used in digital technology of milled and printed stabilizer splints can influence fracture resistance and microorganism adhesion, in detriment of the resin applied in manufacture of conventional thermopolymerizable splints and if the tested properties are related to thickness variation of these devices. The method included mechanical and microbiological steps, each one composed by Conventional (CG) (n=30), Milled (MG) (n=30) and Printed (PG) (n=30) groups, according to the method of preparation, each one having three subgroups (n=10) that varied the specimen thickness from 1 to 3 mm. In the mechanical step, the samples, in the form of 65 mm bars, were tested for fracture resistance in a universal testing machine, with load cell of 500 kgf and speed of 1 mm/min; in the microbiological step, the shape was in form of 15 mm diameter discs, subjected to microorganism adhesion to the surface with exposure to Streptococcus mutans and kept for 24 hours at 35 °C in oven for successive CFU counting, with positive control. The tests were performed in triplicate and data were stored in SPSS 22.0 and statistical analysis used ANOVA and Tukey's post hoc. In the results of mechanical step ANOVA had identified statistically significant differences between the groups (p≤0,005), showing CG and MG had presented better results. Tukey´s post hoc had considered statistically significant difference between MG and PG (p=0,031), listing MG as superior. For the microbiological step, they did not show statistical differences between the groups (p>0.005) in any analysis. It was observed milled resins described superior results and/or close to the conventional technique one, for fracture resistance; and resins of digital and conventional technique, regarding the microorganism adhesion to the surface, did not differ from each other (AU).

The Effect of Coloring Beverages on Color Stability of Hybrid Ceramics with Different Surface Treatments

ABSTRACT Objective To assess the effects of coloring beverages on the color stability of two types of hybrid ceramics with different surface treatments. Material and Methods 180 specimens of two hybrid ceramics (Vita Enamic and Mazic Duro) and a feldspathic ceramic (Vita Mark II) were prepared (n=60 in each group). Half of the discs in each group were glazed while the other was polished. The specimens were then divided into three subgroups and immersed in distilled water, carrot juice, and coffee. The overall color difference (∆E) was calculated based on CIE L*a*b* color space. Data were analyzed using three-way and one-way ANOVA; Tukey's honest significant difference was also done for pairwise comparisons (α=0.05). Results Vita Mark II specimens revealed less overall color changes compared to other groups. The ∆E of the glazed Vita Enamic specimens was greater than polished specimens following immersion in distilled water (p=0.03) and coffee (p=0.001), but it was not significant for carrot juice. The same results were obtained for polished Mazic Duro specimens. Relatively similar amounts of ∆E were recorded in polished and glazed subgroups of Vita Mark II. Conclusion The ∆E of hybrid ceramics was higher than Vita Mark II. Polishing could be recommended for surface treatment of hybrid ceramics instead of glazing, saving time and facilitating the process.

Comparison of Bracket Position Accuracy with Different CAD/CAM Indirect Bonding Systems

ABSTRACT Objective To evaluate the accuracy of three different digital bracket positioning systems, comparing vertical, mesiodistal and buccolingual accuracy. Material and Methods The same case was sent to Orapix, Insignia, and Orthocad systems and the brackets were bonded to the malocclusion models.Damon 3 MX brackets were used with all systems and the brackets were bonded to the models with the same bonding protocol and materials. The comparison of the position of each single bracket was made with digital photography, and ImageJ software was used to find the length in pixels and then convert it to hundredths of a mm for vertical, mesiodistal and buccolingual displacement, compared to the setup. Results Insignia System reported the average higher vertical displacement (0.28 mm), compared with the other two appliances (0.22-0.23 mm), and showed the lowest average displacement for the mesiodistal and buccolingual positioning (0.14 and 0.07 mm, respectively).However, these slight bracket positioning variations between these bonding systems were not statistically different (p>0.05). Conclusion The three systems analyzed were shown to be accurate in positioning the brackets, and none of them was statistically better.

Desempenho clínico de laminados cerâmicos em zircônia ultratranslúcida: ensaio clínico controlado e randomizado / Clinical performance of ultratranslucent zirconia ceramic laminates: randomized controlled clinical trial

Objetivo: Avaliar a sobrevida clínica de laminados cerâmicos em zircônia ultratranslúcida e os impactos desse tratamento na qualidade de vida do paciente. Materiais e métodos: O estudo é um ensaio clínico controlado e randomizado, duplo cego (paciente e avaliador) e de caráter longitudinal. A amostra foi de 82 laminados cerâmicos: 39 laminados em dissilicato de lítio para o grupo controle e 43 em zircônia ultratranslúcida para o grupo experimental. O tratamento restaurador foi realizado por cirurgiões-dentistas participantes do projeto de extensão "Próteses Fixas Metal-Free". A coleta de dados foi realizada por um único examinador nos períodos de avaliação de 1 mês (T1), 6 (T2), 12 (T3), 24 (T4), 36 (T5) e 48 (T6) meses. Quanto ao impacto na qualidade de vida, um questionário modificado OIDP (Oral Impact of Daily Performances) foi usado. A análise da longevidade clínica foi feita através dos critérios modificados de Ryge conferidos com espelho clínico e explorador. Os dados referentes a sobrevida dos laminados de diferentes materiais foram representados graficamente através da curva de Kaplan-Meier. Os escores dos critérios de Ryge, e impacto na qualidade de vida do paciente foram a analisados descritivamente. As espessuras médias para cada terço (cervical, medial e incisal) foram comparadas entre os diferentes materiais através do teste Anova 1 fator. Para análise estatística o nível de significância estabelecido foi de 5%. Resultados: A taxa de sobrevida clínica foi de 100% para os laminados de ambos os materiais. Apenas o critério descoloração marginal obteve uma classificação diferente de A. O escore B foi apresentado por 9 laminados de dissilicato de lítio e 2 de zircônia ultratranslúcida, Não houve nenhuma interferência negativa do tratamento na qualidade de vida dos indivíduos. Falar e relaxar foram as atividades em que o tratamento menos interferiu. Não houve diferença estatisticamente significante para as espessuras dos laminados entre os dois tipos de materiais. Conclusão: O tratamento com laminados confeccionados em zircônia ultratranslúcida apresenta desempenho clínico similar aos casos tratados em dissilicato de lítio (AU).

Objective: to evaluate the clinical survival of ceramic laminates in ultra-translucent zirconia and the impacts of this treatment on the patient's quality of life. Materials and methods: The study was analyzed as a controlled, randomized, double-blind (patient and evaluated) clinical trial with a longitudinal character. The sample studied was 82 ceramic laminates divided into two groups according to the type of material, 39 laminates in lithium disilicate for the control group and 43 in ultra-translucent zirconia for the experimental group. The restorative treatment was carried out by dentists participating in the extension project "Metal-Free Fixed Prostheses". Data collection was performed by a single examiner in the evaluation periods of 1, 6, 12, 24, 36 and 48 months. For the impact on quality of life, a modified OIDP (Oral Impact of Daily Performance) was used. An analysis of clinical longevity was performed using Ryge's modified criteria with a clinical mirror and explorer. The data on the survival of laminates of different materials were plotted using the Kaplan-Meier curve. The Ryge criteria scores and impact on the patient's quality of life were descriptively arranged. The thicknesses for cervical, medial and incisal were compared between the different materials using the ANOVA One-Way test. For statistical analysis, the level of significance was set at 5%. Results: The clinical survival rate was 100% for the laminates of both materials. Only the discoloration marginally criterion obtained from a classification other than A. The B score was presented by 9 laminates of lithium disilicate and 2 of ultra-translucent zirconia. There was no negative interference from treatment on the quality of life. Talking and relaxing were activities in which the treatment least interfered. No statistically significant difference for laminate thickness between the two materials. Conclusion: The treatment with laminates made of ultratranslucent zirconia has clinical performance similar to the cases treated with lithium disilicate (AU).

Influência dos diferentes fluxos de trabalho CAD/CAM na precisão e qualidade dos contatos proximais e oclusais em coroas de dissilicato de lítio / Influence of different CAD/CAM workflows on the accuracy and quality of proximal and occlusal contacts in lithium disilicate crowns

Esse estudo in vitro objetivou avaliar o efeito do fluxo de trabalho digital utilizando diferentes sistemas CAD/CAM (Chairside e InLab) na precisão de coroas de dissilicato de lítio quanto à reprodutibilidade e qualidade dos contatos oclusais e proximais. Foram confeccionadas coroas de dissilicato de lítio (n=50), em que mensurou-se três fluxos de trabalho CAD/CAM Chairside ­ CEREC Bluecam (n=10), CEREC Apollo Di ­ CAI (n=10) e 3Shape TRIOS ­ (n=10) ­ e dois fluxos de trabalho CAD/CAM inlab ­ CEREC InEos X5 ­ (n=10) e 3Shape D900 (n=10). Para a avaliação dos contatos, coroas foram projetadas virtualmente; imagens dos contatos oclusais e proximais oferecidas pelo software dos sistemas; capturadas e pareadas com as imagens reais dessas coroas após a fresagem e fixação com elastômero intencionando simular a cimentação e checagem dos contatos por meio de carbono. As imagens foram inseridas em um software de forma randomizada e avaliadas por três avaliadores, calibrados e blindados usando de questionários com scores e escala visual analógica (EVA). Utilizou-se, ainda, o Teste Kruskal-Wallis e o Pós-teste de Mann Whitney com penalização de Bonferroni (significância estatística de 0,0083) para a comparação dos contatos nas proximais, simulando clinicamente (real) versus os contatos virtualmente apresentados pelos sistemas, havendo diferenças estatisticamente significantes (p<0,001). Os sitemas Bluecam (M= 6.48) e ApolloDi (M=6.15) apresentaram valores médios melhores em relação ao Ineos (M=3.65) e 3Shape D900 (M=3.41). O TRIOS (M=4.60) obteve avaliação similar a ambos. No que concerne à comparação dos contatos oclusais das coroas simulando clinicamente (real) versus os contatos virtualmente apresentados pelos sistemas, usou-se ANOVA e Pós-teste de Tahame. Houve diferença estatisticamente significativa (p= 0.002) entre o sistema TRIOS (M=7.99) e os sistemas Ineos (M=6.78) e 3Shape D900 (M=6.94), assim como entre os diferentes sistemas chairside e Inlab (p<0,001) na avaliação dos contatos oclusais após checagem por meio de carbono, simulando uma situação clínica usando o teste ANOVA e Pós-teste de Tukey (Bluecam M= 7.89; ApolloDi M= 7.27; TRIOS M= 7.41; 3Shape D900 M= 6.90 e Ineos M= 4.09). Resultado semelhante foi observado na avaliação qualitativa desses contatos oclusais, no qual foi aplicado o teste de Qui-Quadrado na categoria Excelete/Bom para os sistemas Bluecam (93,3%), ApolloDi (73,3%), TRIOS (86.7%) e 3Shape D900 (70 %), e na categoria Deficiente o Ineos (93,3%). O teste de Qui-Quadrado também foi empregue na análise da qualidade clínica dos contatos proximais por meio do uso do fio dental. Assim, 50% das coroas apresentaram deficiência do contato, com ausência de ponto de contato. Apenas o sistema TRIOS apresentou 75% na categoria Excelente/Bom. Dentro das limitações do estudo, conclui-se que os sistemas Chairside mostraram melhores resultados quando comparados aos sitemas InLab na reprodução dos pontos de contatos oclusais e proximais identificados no programa virtual com os contatos reais após fresagem e fixação das coroas, simulando uma situação clinica; e melhor acurácia na qualidade dos contatos oclusais e proximais comparados aos sitemas InLab, que apesar de apresentarem resultados inferiores também foram favoráveis (AU).

The purpose of this in vitro study was to evaluate the effect of the digital workflow using different CAD / CAM systems (Chairside and InLab) in lithium disilicate crowns, regarding the reproducibility and the quality of occlusal and proximal contacts. Lithium disilicate crowns were produced (n=50) and divided into the following groups: -Three chairside CAD / CAM workflows: CEREC Bluecam (n = 10), CEREC Apollo Di CAI (n = 10), 3Shape TRIOS (n = 10) and two InLab CAD / CAM workflows: CEREC InEos X5 (n = 10) and 3Shape D900 (n = 10). Images of occlusal and proximal contacts calculated from virtual models were compared to images of real contacts, identified through carbon, in milled crowns that were fixed with elastomer to simulate cementation. The images were inserted into a software in a randomized way and evaluated by 3 blind and calibrated evaluators through questionnaires and a visual analogue scale (VAS). The Kruskal-Wallis Test and the Mann Whitney Post-test with Bonferroni corrections (statistical significance of 0.0083) were used to compare the proximal contacts of the clinically simulated crowns and the proximal contacts of the virtual crowns. Statistically significant differences (p <0.001) were found, in which the Bluecam (M = 6.48) and ApolloDi (M = 6.15) systems obtained better mean values compared to Ineos (M = 3.65) and 3Shape D900 (M = 3.41). TRIOS (M = 4.60) obtained similar results to both groups. The occlusal contacts were compared trough ANOVA and Tahame Post-test. There was a statistically significant difference (p = 0.002) between the TRIOS (M = 7.99) system and the Ineos (M = 6.78) and 3Shape D900 (M = 6.94) systems. There was also a statistically significant difference between the different chairside and InLab systems (p <0.001) in the occlusal contacts evaluation with carbon, using the ANOVA test and Tukey's post-test (Bluecam M = 7.89; ApolloDi M = 7.27; TRIOS M = 7.41; 3Shape D900 M = 6.90 and Ineos M = 4.09). A similar result was observed in the qualitative assessment of these occlusal contacts, using the Chi-Square test, in the category Excellent / Good for Bluecam systems (93.3%), ApolloDi (73.3%), TRIOS (86.7%) and 3Shape D900 (70%) and in the Deficient category, Ineos (93.3%). The Chi-Square test was also used to analyse the clinical quality of proximal contacts, using dental floss and 50% of the crowns had contact deficiency, with no contact point. Only the TRIOS system presented 75% of their crowns categorized as Excellent / Good. Within the limitations of the study, it was concluded that the Chairside systems showed better results when compared to the InLab systems in reproducing the virtual occlusal and proximal contact points in the real contacts after milling and fixing the crowns, simulating a clinical situation. Chairside systems also showed better accuracy in the quality of occlusal and proximal contacts compared to InLab systems, which, despite presenting inferior results, were also satisfactory (AU).

Desempenho clínico de coroas monolíticas posteriores de cerâmica infiltrada por polímero: ensaio clínico controlado e randomizado duplo cego / Clinical performance of posterior monolithic polymer-infiltrated ceramic crowns: double-blind randomized controlled clinical trial

Objetivo: avaliar por meio de um ensaio clínico controlado, randomizado e duplo-cego, o desempenho clínico de coroas monolíticas unitárias posteriores confeccionadas em cerâmica infiltrada por polímero, bem como o impacto da reabilitação na satisfação estética e qualidade de vida dos pacientes. Materiais e Métodos: Um total de 20 pacientes que receberam 36 coroas foram incluídos neste estudo. Todos os pacientes assinaram o termo de consentimento livre e esclarecido (TCLE). Os dentes sob reabilitação foram alocados por meio de um sorteio simples entre os grupos: Grupo Controle: (LD- dissilicato de lítio) e grupo Experimental (PIC -Vita Enamic/Vita Zahnfabrik). Registros fotográficos, radiográficos e informações clínicas foram coletados antes, durante e após a reabilitação. As coroas foram avaliadas quanto à taxa de sobrevida clínica (Critérios de USPSH modificados), satisfação estética (escala visual analógica- EVA), qualidade de vida (Oral Impacts on Daily Performances -OIDP), e tipo de falhas (biológicas e técnicas). A coleta de dados foi realizada por um único examinador calibrado e cego para o tipo de material, nos tempos de seguimento T0 (antes do início do tratamento), T1 (1 mês), T2 (6 meses) e T3 (12 meses). O OIDP e os critérios de USPHS foram analisados descritivamente. A satisfação estética foi analisada com MannWhitney/Teste de Friedman/ pós-testes de Wilcoxon. A análise de sobrevivência foi feita usando Kaplan-Meier seguido do teste de log-rank. O nível de significância foi estabelecido em (5%). Resultados: 36 coroas foram colocadas em 20 pacientes com uma média de idade de 47.17 anos (±13,91), sendo 22 (56,4%) coroas do grupo controle (LD) e 14 (35,9%) para o grupo experimental (PIC). A análise de Kaplan-Meier revelou uma taxa de sobrevida de 83,5% para PIC e de 86,2% para LD sem diferenças significativas entre eles (P>0.05). Quatro falhas foram registradas, 2 em cada grupo, sendo dois descolamentos, uma de PIC após 1 mês e uma de LD após 6meses. Houve também uma fratura do dente (LD) e mobilidade grau III (PIC) após 12 meses de acompanhamento. Não houve diferença significativa na satisfação estética, entre o grupo controle e grupo experimental (Mann-Whitney - P>0.05). A satisfação estética foi significativamente maior após 1(T1), 6(T2) e 12(T3) meses quando comparado ao baseline (T0) (Teste de Friedman - P<0.05). A reabilitação com coroas unitárias impactou positivamente na qualidade de vida dos pacientes. Conclusão: Este estudo demonstra que coroas monolíticas unitárias de PIC apresentaram desempenho clínico, estético e um impacto positivo na qualidade de vida dos pacientes após 12 meses, similar ao LD (AU).

Objective: To evaluate, through a controlled, randomized and double-blind clinical trial, the clinical performance of posterior single monolithic crowns made ceramic infiltrated polymer, as well as the impact of rehabilitation on patients' aesthetic satisfaction and quality of life. Materials and Methods: A total of 20 patients who received 36 crowns were included in this study. All patients signed an informed consent form. The teeth under rehabilitation were allocated using a simple draw between the groups: Control Group: (LD- lithium disilicate) and Experimental group (PIC -Vita Enamic). Photographic, radiographic, and clinical information records were collected before, during, and after rehabilitation. The crowns were assessed for clinical survival rate (modified USPSH criteria), aesthetic satisfaction (visual analog scale - VAS), quality of life (Oral Impacts on Daily Performances - OIDP), and type of failures (biological and technical). Data collection was performed by a single examiner calibrated and blinded to the type of material, at the follow-up times T0 (before the start of treatment), T1 (1 month), T2 (6 months), and T3 (12 months). The OIDP and USPHS criteria were analyzed descriptively. Aesthetic satisfaction was analyzed with the Man-Whitney/Friedman test/Wilcoxon post-tests. Survival analysis was performed using Kaplan-Meier followed by the log-rank test. The level of significance was set at (5%). Results: 36 crowns were placed on 20 patients (17 women and 3 men) with a mean age of 47.17 years (± 13.91), with 22 (56.4%) crowns from the control group (LD) and 14 (35.9%) for the group experimental (PIC). The Kaplan-Meier analysis revealed a survival rate of 83.5% for PIC and 86.2% for LD with no significant differences between them (P>0.05). Four failures were recorded, 2 in each group, two detachments after 1(PIC) and 6 months (LD), a tooth fracture (LD), and grade III mobility after (PIC) 12 months of follow-up. There was no significant difference in aesthetic satisfaction between the control group and the experimental group (Mann-Whitney, P>0.05). Aesthetic satisfaction was significantly higher after 1 (T1), 6 (T2), and 12 (T3) months when compared to baseline (T0) (Friedman test - P <0.05). Rehabilitation with single crowns had a positive impact on patients' quality of life. Conclusion: This study demonstrates that single monolithic crowns of PIC presented a good clinical, aesthetic performance and a positive impact on patients' quality of life after 12 months, similarly to PIC (AU).

The Using Virtual Computer-Assisted Planning in Orthognathic Surgery: A Systematic Review and Meta-Analysis

Abstract Objective: To use virtual computer-assisted planning in orthognathic surgeries through meta-analysis and systematic review. Material and Methods: This search took place between 2010 and 2019. The databases searched in this domain included MEDLINE, PubMed, Cochrane Library, Embase, ISI, and Google scholar. Accordingly, the abstracts of the articles were initially reviewed and the ones that had the most coordination with the study objectives were selected. Then, the full texts of the articles were examined; and finally, five studies were selected. In addition to reviewing the related literature, the results were extracted and entered into the meta-analyzer Stata V.14 to summarize the final results. Results: The sample size in this study was at a range from 6 to 28 patients and a total number of 85 patients had participated in the given investigations. As well, CT and CBCT were selected as imaging methods. Clinical imaging and analysis were also employed in computer-assisted planning in all five studies. Subsequently, surgical planning was performed and the virtual splint was designed while the planning time was 225 minutes and 145 minutes in two studies. Conclusion: The present results supported computer-assisted planning and the quality of scientific evidence.

Simulador de dreno de tórax: desenvolvimento de modelo de baixo custo para capacitação de médicos e estudantes de medicina / Chest tube simulator: development of low-cost model for training of physicians and medical students

RESUMO Objetivo: criar, em impressora 3D, um simulador de baixo custo de caixa torácica humana que permita a reprodução da técnica de drenagem fechada de tórax (DFT) comparando sua eficácia com a do modelo animal. Métodos: foi realizada impressão 3D do arcabouço ósseo de um tórax humano a partir de uma tomografia de tórax. Após a impressão das costelas, foram realizados testes com diversos materiais que contribuíram para formar a simulação da caixa torácica e da pleura. Foi, então, realizado um estudo experimental, randomizado e controlado comparando sua eficácia ao modelo animal no ensino da DFT para estudantes de medicina, que foram divididos em dois grupos: Grupo Modelo Animal e Grupo Modelo Simulador, que treinaram DFT em animais e no modelo simulador, respectivamente. Resultados: a reconstrução do tórax exigiu o conhecimento anatômico para análise da tomografia e para edição fiel da superfície 3D. Não houve diferença significativa quanto à segurança de realizar o procedimento entre os grupos (7,61 vs. 7,73; p=0,398). Foi observada maior pontuação no grupo modelo simulador para uso como material didático e aprendizado da técnica de drenagem torácica quando comparado ao grupo modelo animal (p<0,05). Conclusão: o custo final para a confecção do modelo foi inferior ao de um simulador comercial, o que demonstra a viabilidade do uso da impressão 3D para esse fim. Além disso, o simulador desenvolvido se mostrou equivalente ao modelo animal quanto à simulação da técnica de drenagem para aprendizado prático e houve preferência pelo modelo simulador como material didático.

ABSTRACT Objective: by using a 3D printer, to create a low-cost human chest cavity simulator that allows the reproduction of the closed chest drainage technique (CCD), comparing its effectiveness with that of the animal model. Methods: it was made a 3D printing of the bony framework of a human thorax from a chest computerized tomography scan. After printing the ribs, we performed tests with several materials that contributed to form the simulation of the thoracic cavity and pleura. An experimental, randomized, and controlled study, comparing the efficacy of the simulator to the efficacy of the animal model, was then carried out in the teaching of CCD technique for medical students, who were divided into two groups: animal model group and simulator model group, that trained CCD technique in animals and in the simulator model, respectively. Results: the chest reconstruction required anatomical knowledge for tomography analysis and for faithful 3D surface editing. There was no significant difference in the safety of performing the procedure in both groups (7.61 vs. 7.73; p=0.398). A higher score was observed in the simulator model group for "use as didactic material" and "learning of the chest drainage technique", when compared to the animal model group (p<0.05). Conclusion: the final cost for producing the model was lower than that of a commercial simulator, what demonstrates the feasibility of using 3D printing for this purpose. In addition, the developed simulator was shown to be equivalent to the animal model in relation to the simulation of the drainage technique for practical learning, and there was preference for the simulator model as didactic material.

Vertical and horizontal misfit analysis of 3-unit fdp fabricated with different techniques and cad/cam systems

Abstract The aim of this is was evaluate the vertical and horizontal marginal adaptation of 3-unit fixed partial denture frameworks fabricated using different techniques and CAD/CAM systems. A total of 40 framework specimens were fabricated and divided into four groups as follows: lost-wax casting (G1); lost-wax casting with welding (G2); extraoral optical scanning of models (3S/DWOS) (G3); intraoral optical scanning (Cerec Bluecam/Sirona) (G4). A reference model was used to simulate a fixed partial denture with three elements (with a central pontic). The frameworks of G1 and G2 were cast in nickel-chromium (NiCr) alloy, whereas those of G3 and G4 were milled in zirconia. In all groups, vertical and horizontal marginal adaptation (over-contour and under-contour) was evaluated using a three-dimensional optical microscope (Quick Scope, Mitutoyo). The results showed higher vertical marginal misfit in G1 than in the other groups (p<0.001). Regarding horizontal marginal misfit, higher over-contour values occurred in G3 than in the other groups (p<0.001). G3 did not show under-contour at all, whereas the other groups did not differ from each other in this regard (p>0.05). Within the limitations of this study, it can be concluded that lost-wax casting with welding is a viable alternative to the use of CAD/CAM systems to fabricate frameworks of three-unit FPDs, since the techniques yielded similar vertical misfit values. Extra-oral CAD/CAM systems showed the highest horizontal misfit (over-contour) compared to other groups.

Resumo O objetivo deste estudo foi avaliar a adaptação marginal vertical e horizontal de infraestruturas de prótese fixas de três elementos confeccionadas por diferentes técnicas e diferentes sistemas CAD/CAM. Um total de 40 infraestruturas foram confeccionadas e divididas em quatro grupos: fundição por cera perdida (G1); fundição por cera perdida com ponto de solda (G2); escaneamento óptico extraoral para escaneamento do modelo (3S/DWOS); escaneamento óptico intraoral (Cerec Bluecam/Sirona) (G4). Uma matriz metálica foi utilizada para simular uma prótese fixa de três elementos (com pôntico central). As infraestruturas do G1 e G2 foram fundidas em liga metálica de níquel-cromo (NiCr), enquanto que as infraestruturas de G3 e G4 foram fresadas em zircônia. Todos os grupos foram analisados quanto à adaptação marginal vertical e horizontal (sobrecontorno e subcontorno) em microscópio óptico tridimensional (Quick Scope, Mitutoyo). Os resultados apresentaram maiores valores de desadaptação marginal vertical no G1 comparados aos outros grupos (p<0,001). Em relação a desadaptação marginal horizontal, maiores valores de sobrecontorno foram observado no G3 em comparação com os demais grupos (p<0,001). Não foi observado valores de subcontorno para o G3, enquanto que os demais grupos não apresentaram diferença significante para o subcontorno (p> 0,05). Dentro das limitações do presente estudo, pode-se concluir que a técnica convencional após ponto de solda é uma alternativa viável para confecção de infraestruturas de próteses fixas de três elementos comparado ao uso de sistemas CAD/CAM, uma vez que as técnicas apresentaram valores de adaptação marginal vertical similares. Os sistemas CAD/CAM extraoral apresentou o maior desajuste horizontal (sobrecontorno) em comparação com outros grupos.

Comparação da adaptação marginal de coroas totais confeccionadas em sistemas CAD/CAM em relação às confeccionadas em outras técnicas / Comparison of marginal adaptation of full crowns manufactured using CAD/CAM compared to those obtained through other techniques

Os sistemas CAD/CAM estão cada vez mais difundidos na área odontológica e vem conquistando uma gama maior de adeptos, desde o seu surgimento há 40 anos, talvez devido às vantagens inerentes ao sistema, que aperfeiçoa o trabalho laboratorial e reduz o tempo clínico do cirurgião dentista. Um dos aspectos mais relevantes para optar-se pela técnica CAD/ CAM, ou pela técnica da cera perdida ou pela técnica slip cast é a adaptação marginal que se consegue obter quando da confecção da peça protética. A ocorrência de falhas altera a longevidade do trabalho protético, assim como a do elemento dentário remanescente. Esta revisão tem por objetivo comparar a adaptação cervical de coroas totais confeccionadas por sistemas CAD/CAM com coroas totais confeccionadas pela técnica da cera perdida ou pela técnica slip cast. Foram selecionados e analisados 22 artigos nas bases de dados Pubmed e Scielo, nos quais 12 sistemas de CAD/CAM diferentes foram encontrados. Variáveis como próteses múltiplas x unitárias, tipo de preparo, estrutura, ajuste interno, cimentação e método de avaliação de adaptação marginal foram analisadas. Na maioria dos artigos revisados houve uma grande discrepância entre as desadaptações com métodos semelhantes variando entre 9µm (Sistema Pocera-Nobel Biocare) e 192 µm (Sistema Cerec-Sirona). Um gap marginal de 56,55 µm (Cerec-Sirona) foi encontrado em outro estudo, usando uma metodologia diferente. Entende-se que mais estudos, com uma metodologia padronizada, devem ser realizados.

The CAD/CAM systems are becoming increasingly widespread in Dentistry and have gained a wider range of fans, from its inception 40 years ago, perhaps due to the advantages inherent in the system, which optimizes the laboratory work and reduces clinical time of the dentist. One of the most relevant aspects to choose the CAD/CAM technique or the technique of lost wax or slip cast by technical aspects is marginal fit obtained. The occurrence of failures on the marginal fit compromises the longevity of prosthetic work, as well as the remaining tooth. This review aims to compare the cervical adaptation of crowns made by CAD/CAM systems with crowns made by the lost wax technique by technique or slip cast. A search was performed in Pubmed and SciELO databases and 22 articles were selected and analyzed, and 12 different CAD/CAM systems were found. Variables such as multiple vs. single prostheses, type of preparation, structure, internal adjustment, cementation and method applied to assess marginal adaptation were analyzed. Most papers registered a large discrepancy between the mismatches with similar methods ranging from 9µm (Pocera-Nobel Biocare System) to 192 µm (Sirona-Cerec System). A marginal gap 56.55 µm (Sirona-Cerec) was found in another study using a different methodology. It is understood that further studies with a standardized methodology should be performed.

Tratamento estético de diastemas múltiplos com facetas pelo sistema CAD-CAM / Aesthetic rehabilitation of multiple diastemas using veneers produced through CAD-CAM system

Facetas minimamente invasivas, também conhecidas como ôlentes de contatoõ, têm sido consideradas uma alternativa interessante para tratar problemas estéticos nos dentes anteriores. O presente relato de caso descreve passo a passo o tratamento de diastemas múltiplos com facetas minimamente invasivas, e discute tópicos importantes relacionados a este assunto quanto a indicações, materiais utilizados e longevidade destes tipos de restaurações...

Minimally invasive veneers, also known as ôcontact lensesõ, are being considered an interesting alternative for aesthetic rehabilitation of anterior teeth. This case report describes, step by the step the treatment of multiple diastemas with minimally invasive veneers, and addresses important issues related to this topic concerning indications, materials and longevity of these type of restorations...

Aplicação de modelagem molecular e de formalismo do CAMD (Computer-Aided Molecular Design) na elucidação do mecanismo de ação de inibidores de metalopropteinases de matriz / Molecular modeling methods and computer-aided molecular design (CAMD) formalisms for elucidating the mechanism of action of matrix metalloproteinases inhibitors

As metaloproteinases de matriz (MMP) são enzimas superexpressas em quase todos os tumores humanos, sendo que os subtipos MMP-2 e MMP-9 têm sido associados ao potencial metastático e prognóstico desfavorável em neoplasias malignas como, por exemplo, melanoma metastático e glioma. Compostos capazes de inibir a atividade destas enzimas podem representar potenciais agentes terapêuticos. O composto 4-nerolidilcatecol (4-NC), isolado de plantas do gênero Pothomorphe, apresentou resultados promissores para o tratamento do melanoma e glioma e foi capaz de atuar em várias etapas bioquímicas importantes envolvidas na progressão dessas patologias, inclusive inibindo MMP-2 e MMP-9. No entanto, o mecanismo de ação do 4-NC não está completamente elucidado. O presente estudo envolveu a aplicação de métodos de modelagem molecular e de formalismos do planejamento de novas moléculas auxiliado por computador, CAMD (Computer-Aided Molecular Design) a fim de explorar a interação entre esta molécula e as enzimas MMP-2 e MMP-9, além de planejar novos inibidores para estes alvos. Análise exploratória de dados, que compreende a análise de agrupamentos hierárquicos e de componentes principais. foi desenvolvida para um conjunto de hidroxamatos (N=64) descritos como inibidores de MMP-2 e MMP-9, a fim de identificar as propriedades moleculares que mais influenciavam o processo de discriminação dos compostos. As propriedades termodinâmicas, eletrônicas e estéricas foram importantes para descrever os compostos mais ativos no conjunto de dados da MMP-2. Para a MMP-9, o coeficiente de distribuição (ClogD) em pH 1,5 foi relevante no processo de discriminação do conjunto. A presença de substituintes volumosos na porção R3 parece ser crucial para o conjunto de inibidores investigados. Esta região está envolvida em interações moleculares com a cavidade S1 de ambas as enzimas, mas há um limite de volume a ser considerado para estes substituintes. O formalismo QSAR-4D independente do receptor (IR) foi aplicado ao mesmo conjunto de dados e permitiu estabelecer o mapeamento do farmacóforo, além de explorar diferentes alinhamentos para a obtenção da hipótese de conformação bioativa prevista pelo melhor modelo de QSAR. OS modelos QSAR apresentaram boa capacidade de previsão, auxiliaram na proposição de novos inibidores e estimaram a atividade do 4-NC. Com o melhor modelo QSAR para MMP-9 (N=64), a atividade prevista para o 4-NC foi classificada na faixa dos inibidores com atividade moderada. Entretanto, o melhor modelo QSAR obtido para MMP-2 (N=38) não foi capaz de prever, de forma adequada, a atividade de compostos com arcabouço químico diferente daqueles utilizados na construção dos modelos. Estudos de ancoramento molecular foram desenvolvidos para investigar a orientação do 4-NC no sitio catalítico das duas enzimas e as interações que poderiam ser estabelecidas nestes complexos. Duas conformações favoráveis foram encontradas. Simulações computacionais de dinâmica molecular foram desenvolvidas com os complexos mais promissores selecionados nos estudos de ancoramento, a fim de obter informações mais detalhadas e de maior confiabilidade. sobre suas interações intermoleculares. O 4-NC tende a se orientar no sítio de forma a acomodar sua cadeia lateral no bolso S1 adjacente ao sítio catalítico em ambas as enzimas. Ensaios de zimografia também foram realizados com o objetivo de elucidar possíveis contribuições da cadeia lateral e do núcleo catecólico do 4-NC na atividade inibitória frente às enzimas em estudo. O núcleo catecólico parece ser o responsável por sua atividade, pois o composto 1,2dimetoxibenzeno, que possui as hidroxilas bloqueadas por grupos metil, não foi capaz de exercer atividade inibitória significante frente à MMP-2 e MMP-9. Estudos de voltametria reforçaram a hipótese de que o 4-NC tem a capacidade de quelar os íons zinco presentes no tampão de incubação

Matrix metalloproteinases (MMP) enzymes are overexpressed in almost all human tumors, and MMP-2 and MMP-9 subtypes have been associated with metastatic potential and poor prognosis in malignant tumors, such as metastatic melanoma and glioma. Compounds capable of inhibiting the activity of theses enzymes would be considered as potential therapeutic agents. The 4-nerolidylcatechol compound (4-NC), isolated from plants of genus Pothomorphe, has showed promising results in the treatment of melanoma and glioma, and was able to act in several important biochemical steps involved in the progression of these diseases, as well as inhibiting MMP-2 and MMP-9. However, the 4-NC mechanism of action is not completely understood. This study has involved the application of molecular modeling methods and formalisms of computer-aided molecular design (CAMD) in order to explore the interaction between 4-NC and MMP-2/MMP-9, and to design new inhibitors for these targets. Exploratory data analysis, which comprises hierarchical cluster analysis and principal components analysis, was performed to a set of hydroxamates (N=64). previously reported as MMP-2 and MMP-9 inhibitors, in order lo identify the molecular properties that is most critical for the discrimination process regarding the investigated compounds. The thermodynamic, electronic, and steric properties were: quite important to describe the highly active compounds in the data set of MMP-2, whereas the apparent partition coefficient (ClogD) at pH 1.5 was the property more relevant for MMP-9 data set. The presence of bulky substituents on the R3 moiety seems to be crucial for this set of inhibitors due to the molecular interaction with the S1 subsite of both enzymes. However, there is a limit regarding the substituents volume in this region. Receptor independent (RI) 4D-QSAR analysis was applied lo the same data set and it was possible to establish the pharmacophore mapping, besides to explore different alignments in order to generate the hypothesized bioactive conformation through the best QSAR model. The QSAR models have presented good predictability, assisted in proposing new inhibitors, and estimated the activity of 4-NC. Regarding the best QSAR model for MMP-9 (N=64), the 4-NC predicted activity was classified in the range of the moderate active inhibitors. The best QSAR model obtained for MMP-2 (N=38), however was not able to properly predict the activity for compounds with different chemical scaffold from those used to build up the QSAR model. Molecular docking studies have been developed to investigate the 4-NC binding mode into the catalytic site of the two enzymes and the interactions that could be established in those complexes. The results have shown two favorable conformers regarding the MMP inhibition. Molecular dynamics computational simulation were combined to molecular docking studies in order to obtain more detailed and reliable information regarding the intermolecular interactions of each complex. The 4-NC molecule tends to accommodate the side chain in the S1 pocket adjacent to the catalytic site in both enzymes. Experimental zymography assays were also performed to elucidate the possible contribution of the side chain and the catechol core in the 4-NC inhibitory activity against the MMP-2 and MMP-9 enzymes. The catechol core seems to be responsible for its activity, since the 1,2 dimethoxybenzene compound, which has the hydroxyl blocked by a methyl group, was not able to exert any significant inhibition on enzymes. Voltametric assays confirmed the hypothesis that 4-NC chelates zinc ions present in the incubation buffer

Bond strenght of zirconia submitted to different surface treatments

To evaluate the shear bond strength of a recent adhesive system used in the cementation of zirconia.Material and Methods:Overall, 72 zirconia specimens (Zirconzhan) were divided and randomized into 3 groups according to the type of surface treatment: G1 no treatment + adhesive system; G2 blasted with aluminum oxide + adhesive system and G3 tribochemical treatment (Rocatec Plus) + adhesive system. Half of each group (n = 12) had bond strength evaluated on two occasions: 24 hours after cementation, kept stored in distilled water at 37 ° C without thermal cycling, and after thermal cycling (5000 cycles, 5°C-55°C). Data were analyzed by ANOVA with Tukey's post-test (α≤0.05).Results:At first moment, G1 and G3 showed higher bond strength (8.64 ± 3.43 MPa and 6.55 ± 2.27 MPa) compared to G2, with no statistically significant difference between them. After thermal cycling, G3 showed higher bond strength (7.70 ± 1.82 MPa).Conclusion:Initially, only the adhesive system promoted higher bond strength, but after thermal cycling,bond strength decreased. The best treatment to promote high bond strength to zirconia is to associate tribochemical treatment with the adhesive system; most failures observed after thermal cycling were mixed and cohesive, showing a mechanical imbrication of the adhesive system, suggesting that there is no chemical bond; and the surface of the group with greater bond strength after thermal cycling showed more surface irregularities compared to the other groups...

Desmistificando a evolução dos sistemas cerâmicos / Demystifying the evolution of ceramic systems

Os sistemas cerâmicos apresentam uma incrível evolução na busca implacável pela estética. A união desses sistemas aos metais foi necessária em um primeiro momento para compensar a friabilidade intensa que esses sistemas apresentavam inicialmente. Todo o processo de evolução desse grupo de materiais gira em torno de abrir mão do metal, retirando-os dos processos de reabilitação. O grande impasse é alcançar com as cerâmicas a resistência que o metal proporciona e por isso as pesquisas se concentram em reforçar os sistemas cerâmicos tornando-os capazes de resistir às forças e tensões geradas durante a função mastigatória. O objetivo deste trabalho é relatar esse processo de evolução tornando o entendimento sobre esse tema mais fácil, assim como esclarecer, dentro de uma classificação simplificada, a indicação, o potencial de resistência e grau de translucidez dentre os diversos sistemas. Através do levantamento bibliográfico, pode-se afirmar que atualmente é totalmente possível a realização de restaurações unitárias em qualquer posição no arco dentário. Já para reabilitações com próteses extensas, principalmente na região de molares, essa escolha deve ser bastante criteriosa. Dispomos de sistemas cerâmicos para confecção de copings altamente capazes de resistir à carga, mas estudos clínicos randomizados de longo prazo ainda são necessários para avaliar a vida útil desse tratamento.

Ceramic systems represent an incredible evolution in the search for aesthetics. In a first moment the association of these systems with metals was necessary to compensate its low resistance. The evolution of this group of materials is moving toward giving up the metal material, removing them from the oral rehabilitation. The major objective is to obtain a ceramic with the same resistance provided by the metal and therefore most researches are focused on strengthening the ceramic systems so that they can resist to the pressure generated during masticatory function. The aim of this work is to describe this process of evolution as well as clarify, within a simplified classification, the indication, the resistance and translucency of ceramic systems. Through literature review we can affirm that the realization of single crowns is possible in any position in the dental arch. For extensive rehabilitation with prostheses, especially in the molars region, this choice should be carefully evaluated. Currently, more resistant systems are used to ceramic copings highly capable of load resistance, but randomized clinical trials of long-term are still needed to evaluable the lifetime of the material.

Resolução estética por meio de cirurgia periodontal com reembasamento transcirúrgico e coroas CAD-CAM / Aesthetic resolution through periodontal surgery with trans-surgical reline and CAD-CAM crowns

Atualmente, materiais não metálicos têm sido utilizados apresentando resultados estético-funcionais muito satisfatórios. O planejamento criterioso é fundamental para que resultados favoráveis sejam obtidos. O objetivo desse trabalho é apresentar um caso de reabilitação oral anterossuperior com resolução satisfatória por meio de cirurgia periodontal associada ao reembasamento das coroas provisórias e confecção de coroas CAD-CAM em zircônia (CERCON®)

Currently, non-metallic materials have been used showing satisfactory aesthetic and functional results. A careful planning is essential to obtain favorable results. The aim of this study was to present a clinical case of oral rehabilitation with satisfactory anterosuperior resolution through periodontal surgery associated with reline of temporary crowns and CAD- -CAM zirconia crowns (Cercon®)

Adaptação marginal e interna de coroas de porcelana pelo sistema CAD/CAM / Marginal and internal adaptation of porcelain crowns by CAD / CAM system

Este trabalho discutiu a desadaptação marginal e interna de coroas em porcelana pura, produzidas por sistemas CAD/CAM. Foram selecionadas 13 artigos em inglês, 4 artigos em português e 2 monografias publicados de 2009-2013. De acordo com cada artigo as coroas foram avaliadas: sem cimentação, após cimentação e antes e após cimentação, considerando as variáveis que vão influenciar a desadaptação...