Influence of filling materials on the fracture resistance of resin composite used for sealing screw access hole / Influência dos materiais de preenchimento na resistência a fratura das resinas compostas utilizadas para selamento do orifício de acesso ao parafuso

Introduction: Screw-retained restorations have a screw access hole (SAH) sealed with resin composite aiming at safe-guarding the aesthetic features of the ceramic veneer. The loss or wear of the resin composite applied in sealing the SAH is among the most common complications in implant prosthodontics, as the fracture of ceramic veneer. Objective: Evaluate the influence of sealant materials on the fracture resistance of resin composite applied in sealing screw access hole in screwed (SAH) implants. Material and method: The samples were produced from UCLA abutments in metallic NiCr alloy with subsequent application of ceramic. After asperisation and conditioning ceramic surface, was applied silane and dentin adhesive, before sealing the conduits with resin composites Z100 and P60. Nine groups (n=10) were evaluated: sealing with Z-100 (ZNC) and P-60 (PNC) without obturation of SAH; sealing with Z100 (ZCP) and P-60 (PCP) with absorbent cotton; Z100 (ZPT) and P60 (PPT) with polytetrafluoroethylene; Z100 (ZGP) and P60 (PGP) with gutta-percha and a cemented ceramic crown (ICS). After the fracture resistance test, the data were analyzed using two-way ANOVA and Tukey HSD tests (p<.05). Result: The fracture mode was evaluated by scanning electron microscope. Irrespective of the filling material, the highest mean values of fracture resistance were observed in the sealing with P60 (p=.002). When combined with resins composed of a sealing material, the results obtained were: ZGP: 805.5N/ PGP: 929.5N

Introdução: As próteses parafusadas possuem orifício de acesso ao parafuso (SAH), os quais são selados com resina composta. Sua perda ou desgaste está entre as complicações mais comuns em próteses sobre implantes, associadas a fratura da lâmina cerâmica. Objetivo: Assim, é importante avaliar a influência dos materiais de selamento na resistência à fratura de resina composta aplicada ao SAH no selamento de prótese sobre implantes parafusadas. Material e método: As amostras foram produzidas utilizando pilares UCLA em liga metálica de NiCr com posterior aplicação de cerâmica. Após asperização e condicionamento da superfície cerâmica, foram aplicados silano e adesivo dentinário, antes da selagem dos condutos com as resinas compostas Z100 e P60. Foram avaliados nove grupos (n = 10): selamento com Z-100 (ZNC) e P-60 (PNC) sem selamento do SAH; selamento com Z100 (ZCP) e P-60 (PCP) com algodão absorvente; Z100 (ZPT) e P60 (PPT) com politetrafluoroetileno; Z100 (ZGP) e P60 (PGP) com guta-percha e coroa de cerâmica cimentada (ICS). Após o teste de resistência à fratura, os dados foram analisados usando ANOVA de dois fatores e testes Tukey HSD (p<0,05). O tipo de fratura foi avaliado por microscópio eletrônico de varredura. Resultado Independentemente do material obturador, os maiores valores médios de resistência à fratura foram observados no selamento com P60 (p=0,002). Quando combinados com resinas compostas por um material de selamento, os resultados obtidos foram: ZGP: 805,5N/ PGP: 929,5N

Cytotoxic Effects of Bulk-Fill Composites on L929 Fibroblast Cells / Efeitos citotóxicos dos compósitos bulk-fill em células de fibroblastos L929

Objective: Unlike traditional composite resins, bulk-fill composite resins could be polymerized as thicker layers. This study aims to contribute to the field by investigating the cytotoxic effects of various bulk-fill composite resins on L929 mouse fibroblast cells in vitro. Material and Methods: In our study, six bulk fill and one conventional composite resin were used. Composite resin samples (8×4 mm) were prepared in a sterile cabinet by using a glass mod and polymerizing with a led light device (DTE LUX E, Germany). Composite samples (n:3) of which surface area was calculated according to ISO 10993-12: 2012 standards (3 cm2/ml), were kept in media for 24 h and 72 h in 37 oC incubator, their extracts were filtered in 1:1 and 1:2 proportion and were added on L929 mouse fibroblast cells. Cell viability was examined by the MTT assay and cell death by the LDH test. Cell viability results were evaluated using one-way analysis of variance (ANOVA) test (p<0.05). Results: When the 1:1 extracts from 4 mm thick bulk-fill composite samples were applied on L929 mouse fibroblast cells, cell viability rates showed significant differences compared to the control group at the end of 24 h and 72 h (except for Estelite Bulk Fill Flow). Although the extracts of the tested composite samples at 1:1 and 1:2 ratio at the end of 72 hours caused a decrease in L929 mouse fibroblast cell viability, the cell viability rate of only PRG-containing bulk fill composite and conventional composite remained below the cell viability ratio (70%) specified in ISO standards. Bulk fill composites did not produce toxic effects (except Beautifil Bulk Restorative) according to the LDH test. Conclusions: Despite decreasing in general the cell viability, bulk-fill composite resins used in 4 mm thick layers provided cell viability rates over the acceptability level, except PRG-containing bulk fill composite (Beautifil Bulk Restorative), which was cytotoxic to L929 mouse fibroblasts. (AU)

Objetivo: Ao contrário das resinas compostas tradicionais, as resinas compostas bulk-fill podem ser polimerizadas como camadas mais espessas. Este estudo visa investigar in vitro os efeitos citotóxicos de várias resinas compostas bulk-fill em células de fibroblastos de camundongo L929.Material e Métodos: Em nosso estudo, seis resinas tipo bulk fill e uma resina composta convencional foram usadas. Amostras de resina composta (8 × 4 mm) foram preparadas em gabinete estéril usando um molde de vidro e polimerizado com um dispositivo de luz LED (DTE LUX E, Alemanha). Amostras compostas (n=3) cuja área de superfície foi calculada de acordo com os padrões ISO 10993-12:2012 (3cm2/ml), foram mantidas em meio e incubadas por 24 h e 72 h a 37 ºC, seus extratos foram filtrados na Proporção de 1:1 e 1:2 e foram acondicionados em cultura de células de fibroblastos de camundongo L929. A viabilidade celular foi examinada pelo ensaio MTT e a morte celular pelo teste LDH. Os resultados de viabilidade celular foram avaliados usando o teste de análise de variância (ANOVA) um fator (p <0,05). Resultados: Quando os extratos foram plaqueados na proporção 1:1 de amostras de compósito bulk-fill de 4 mm de espessura com as células de fibroblastos de camundongo L929, as taxas de viabilidade celular mostraram diferenças significativas em comparação com o grupo controle no final de 24 h e 72 h (exceto para Estelite Bulk Fluxo de enchimento). Embora os extratos das amostras compostas testadas na proporção de 1:1 e 1:2 ao final de 72 horas tenham causado uma diminuição na viabilidade das células de fibroblastos de camundongo L929, a taxa de viabilidade celular apenas do compósito de preenchimento total contendo PRG e o compósito convencional permaneceram abaixo a taxa de viabilidade celular (70%) especificada nas normas ISO. Os compósitos de preenchimento a granel não produziram efeitos tóxicos (exceto Beautifil Bulk Restorative) de acordo com o teste de LDH. Conclusão: Apesar de diminuir em geral a viabilidade celular, as resinas compostas bulk-fill usadas em camadas de 4 mm de espessura forneceram taxas de viabilidade celular acima do nível aceitável, exceto o compósito bulk fill contendo PRG (Beautifil Bulk Restorative), que foi citotóxico para fibroblastos de camundongos L929 (AU)

Effect of ultrasonic vibration on microshear bond strength of flowable composite to enamel / Efeito de microcisalhamento com vibração ultrassônica na resistência de união de compósito fluido ao esmalte

Objective: The present study aimed to assess theinfluence of vibration effect on microshear bond strength (µSBS) of flowable composite to enamel. Material and Methods: Sixty non-cariousextracted human premolar teeth were collected and randomly divided into six groups (n = 10) after being trimmed to produce a smooth flat surface: Flowable composites [Wave (SDI), Wave HV (SDI) and Grandioflow (Voco)] were used as bonding agents without or with vibration using an ultrasonic scaler (Mini Piezon, EMS, Switzerland). Composite resin, with an internal diameter of 0.7mm and height of 1mm, was cured on the substrate. The specimens' µSBS was tested by a microtensile tester (Bisco, USA) at a crosshead speed of 0.5 mm/min. The bond strength values were analyzed using one-way ANOVA and post hoc Tukey test (p < 0.05). Results:Vibrationdid not lead to any significant difference in the µSBS values of Wave, Wave HV, and Grandio Flow µSBS values (P=0.690, P=1.000 and P=0.947, respectively). No significant difference was found between flowable composites in terms of micro shear bond strength to enamel (p > 0.05). Conclusions: The application of ultrasonicvibration might not be advantageous in terms of improving the shear bond strength of flowable composites to enamel. (AU)

Objetivo: Este estudo teve como objetivo avaliar a influência de microcisalhamento com efeito de vibração na resistência de união (µSBS) de compósito fluido ao esmalte. Material e Métodos: Sessenta dentes pré-molares humanos extraídos não cariados foram coletados e divididos aleatoriamente em seis grupos (n = 10) após serem desgastados para produzir uma superfície lisa e plana: Compósitos fluidos [Wave (SDI), Wave HV (SDI) e Grandioflow (Voco)] foram usados como agentes adesivos sem e com vibração através de um aparelho ultrassônico (Mini Piezon, EMS, Switzerland). Uma resina composta, com diâmetro interno de 0,7 mm e peso de 1 mm, foi polimerizada no substrato. Os espécimes de µSBS foram submetidos a teste de microtração (Bisco, USA) em uma velocidade de 0.5 mm/min. Os valores de resistência adesiva foram analisados através de testes de ANOVA a um critério e de Tukey post hoc (p < 0.05). Resultados: A vibração não levou a nenhuma diferença significativa nos valores de µSBS entre Wave, Wave HV, e Grandio Flow (P=0.690, P=1.000 e P=0.947, respectivamente). Não foi encontrada nenhuma diferença significativa entre os compósitos fluidos quanto à resistência de união ao esmalte quando sob microcisalhamento (p >0.05). Conclusões: A aplicação de vibração ultrassônica pode não ser vantajosa para uma melhora na resistência adesiva de compósitos fluidos ao esmalte frente a cisalhamento. (AU)

The influence of different surface treatment protocols and bonding agents on the repair microtensile bond strength of six-month' aged composite: An in vitro study / A influência de diferentes protocolos de tratamento de superfície e agentes de união na resistência de união à microtração de reparo de compósito envelhecido por seis meses: um estudo in vitro

Objective: To compare the effect of three surface treatment protocols and two intermediate agents on repairing aged composite, regarding microtensile bond strength (µTBS) and mode of fracture, at two time intervals. Material and methods: Six-monthaged microhybrid composite blocks, were randomly distributed into three groups, subjected to; Fine, Super Fine grit diamond burs or Erbium- Yag Laser surface treatment. Each block had both One Coat bond SL (Bond) and Brilliant Flow flowable composite (Flow) intermediate agents, alongside. Blocks were incrementally repaired using nanohybrid composite, cut into beams, then randomly subjected either immediately (IM) to µTBS test or after thermocycling (TC) for 5000 cycle. Mode of failure was determined using stereomicroscope. Data were analyzed through three-way ANOVA followed by pairwise comparison with Bonferroni correction. Kruskal Wallis test compared groups for failure mode analysis (α=0.05) Results: Super Fine grit showed the highest mean µTBScompared to control for both intermediate agents, IM and after TC at P<0.05. No difference between Fine grit and Laser application for all groups (P>0.05). IM, Bond showed the highest µTBS compared to TC, Flow for all tested groups. Beams roughened with Fine and Super Fine burs showed significantly lower adhesive failures than those roughened with Laser. Flow suffers significantly higher adhesive failure than those with Bond. For TC tested groups; beams with Super Fine bur and Bond showed significantly lower adhesive failure at P=0.029. Conclusion: Super Fine grit and Bond provide the highest µTBS and the least adhesive failure; moreover TC resulted in significant decrease in µTBS (AU)

Objetivo: Comparar o efeito de três protocolos de tratamento de superfície e dois agentes intermediários no reparo de compósito envelhecido, quanto à resistência à microtração (µTBS) e modo de fratura, em dois intervalos de tempo. Material e métodos: Blocos de compósito microhíbrido envelhecidos por seis meses, foram distribuídos aleatoriamente em três grupos, submetidos a; Pontas diamantadas de granulação Fina, Superfina ou tratamento de superfície com laser de Erbio-Yag. Cada bloco tinha ambos os agentes intermediários One Coat bond SL (Adesivo) ao lado de Brilliant Flow (Resina Fluida). Os blocos foram reparados de forma incremental usando compósito nanohíbrido, cortados em palitose, em seguida, submetidos aleatoriamente imediatamente (IM) ao teste de µTBS ou após termociclagem (TC) por 5000 ciclos. O modo de falha foi determinado usando estereomicroscópio. Os dados foram analisados por meio de ANOVA de três fatores, seguida de comparação pareada com correção de Bonferroni. O teste de Kruskal Wallis comparou os grupos para análise do modo de falha (α = 0,05). Resultados: a granulação Super fina apresentou a maior média de µTBS em comparação com o controle para ambos os agentes intermediários, IM e após TC (P <0,05). Não houve diferença entre granulação fina e aplicação de laser para todos os grupos (P> 0,05). IM, Adesivo apresentou a µTBS mais alta em comparação com TC, Resina Fluida para todos os grupos testados. Os palitos asperizados com pontas de granulações Fina e Superfina apresentaram falhas adesivas significativamente menores do que as asperizadas com Laser. Resina Fluida sofreu falhas adesivas significativamente maiores do que aquelas com Adesivo. Para grupos testados TC; palitos tratados com ponta Superfina e Adesivo apresentaram falha adesiva significativamente menor com P = 0,029. Conclusão: a granulação Superfina e o Adesivo fornecem a maior µTBS e o mínimo de falha adesiva; além disso, o TC resultou em uma diminuição significativa da µTBS. (AU)

Efficacy of indine of composite Huaihua fructus posraleae combined with fractional CO2 laser on acral stable vitiligo / 中国基层医药

Objective To OvaluatO thO Officacy and safOty of indinO of compositO Huaihua fructus posralOaO combinOd with fractional CO2 lasOr on acral stablO vitiligo.Methods From OctobOr 2014 to August 2017, 79 casOs with acral stablO vitiligo in thO Sixth POoplO′s Hospital of Dongguan wOrO randomly dividOd into trOatmOnt group and control group according to thO digital tablO. ThO trOatmOnt group(51 casOs) was trOatOd with fractional CO2 lasOr onO timO a month for four timOs, and thO sOcond day was givOn topical indinO of compositO Huaihua fructus posralOaO twicO a day. ThO control group(28 casOs) was trOatOd with topical indinO of compositO Huaihua fructus posralOaO twicO a day. ThO trOatmOnt OffOct was obsOrvOd aftOr trOatmOnt for 3 months and 6 months. Results AftOr trOatmOnt for 3 months and 6 months, thO total OffOctivO ratOs of thO trOatmOnt group wOrO 39.22% , 62.75% ,rOspOctivOly, which wOrO significantly highOr than thosO of thO control group(32.14% , 42.86% ) (χ2 =12.557,18.021,all P<0.05). No sOrious advOrsO OvOnt was obsOrvOd in thO two groups.Conclusion IndinO of compositO Huaihua fructus posralOaO combinOd with fractional CO2 lasOr is safO and OffOctivO in thO trOatmOnt of stablO sporadic vitiligo.

Tijolos leves para alvenaria produzidos a partir de resíduos da indústria madeireira / Lightweight masonry bricks produced from wood industry waste

RESUMO O objetivo deste trabalho foi verificar a possibilidade de utilização de compósitos cimento-madeira na fabricação de componentes leves para alvenaria, visando reduzir os prejuízos ambientais causados pela disposição final da serragem proveniente do desdobro da madeira. Primeiramente foram analisadas as propriedades físicas (teor de umidade, absorção de água, índice de vazios e massa específica) e mecânicas (resistência à compressão e módulo de elasticidade dinâmico) de diferentes traços cimento:areia, cimento:areia:serragem e cimento:serragem. A partir de traços selecionados foram fabricados tijolos maciços de alvenaria com dimensões 90 × 90 × 190 mm, submetidos a ensaios para determinação da massa específica, teor de umidade, absorção de água e resistência à compressão. As propriedades físicas e mecânicas desses componentes foram comparadas com as exigências de normas brasileiras prescritivas referentes a componentes de alvenaria. Foram obtidos resultados satisfatórios, indicando que resíduos da indústria madeireira têm potencial para serem utilizados na produção de componentes leves de alvenaria, podendo ser aplicados como material de construção alternativo.

ABSTRACT The main objective of this work was to investigate the use of cement-wood composites to produce lightweight masonry elements, aiming to reduce environmental damages arising from the disposal of the sawdust originated from wood sawing process. Physical (moisture content, water absorption, void ratio and specific gravity) and mechanical (compressive strength and dynamic Young's modulus) properties of different cement:sand, cement:sand:sawdust and cement:sawdust mix proportions were evaluated. Specific gravity, moisture content, water absorption and compressive strength of 90 × 90 × 190 mm bricks, produced from selected mix proportions, were determined and compared to the requirements of the Brazilian standards for masonry elements. The satisfactory results obtained indicate that lightweight masonry bricks produced with wastes from wood industry have the potential to become an alternative for traditional building materials.

Nova tecnologia aplicada à odontologia minimamente invasiva: relato de caso de remoção de bráquetes ortodônticos / New technology applied to minimally invasive dentistry: a case report of orthodontic brackets removes

O conceito de odontologia minimamente invasiva associado à adesão apresenta uma mudança de filosofia na prática clínica moderna. Os antigos paradigmas de extensão da região a ser restaurada para proteção do remanescente ou aumento da resistência do material restaurador fazem cada vez menos parte da rotina clínica e conceitos de conservação máxima de estrutura dentária tornam-se mais utilizados. Contudo, diante do desenvolvimento de materiais restauradores com propriedades ópticas cada vez mais semelhantes as das estruturas dentárias, definir o limite entre materiais restauradores e estrutura dental tem se apresentando como um desafio. Objetivo: O objetivo deste trabalho é demonstrar a aplicação de um conceito atual baseado na utilização de alta rotação com sistema de iluminação que evidencia o material restaurador diferenciando da estrutura dental para a remoção seletiva de compósitos resinosos utilizados para cimentar bráquetes ortodônticos. Paciente apresentou-se com aparelho ortodôntico fixo em fase final de tratamento, sendo necessária a remoção deste. Após a retirada dos bráquetes ortodônticos, o remanescente de compósito resinoso foi removido com ponta diamantada de granulação fina e extrafina (FG2135 F e FF, KG Sorensen) acoplada em alta rotação que emite luz em comprimento de onda capaz de evidenciar o material restaurador em contraste com a estrutura dentária (Cobra LED Ultra-Vision, Gnatus). Assim, foi possível evidenciar interface entre dente e cimento ortodôntico devido à diferença na fluorescência, resultando assim em maior sensibilidade da técnica e preservação de tecido dentário hígido. Conclusão: Conclui-se que a utilização de alta-rotação capaz de estimular a fluorescência do material restaurador é um método eficaz para remoção de remanescente de compósitos resinosos, sendo uma técnica mais conservadora e menos invasiva.

The concept of minimally invasive dentistry associated to adhesion shows a change in the philosophy of modern clinical practice. The old paradigms of the region extension to be restored to remaining protection or increased resistance of the restorative material are less part of the clinical routine; and maximum conservation of tooth structure concepts become more used. However, in front of the development of restorative materials with optical properties more like to the dental structures, define the limit between restorative materials and tooth structure has been presented as a challenge. The objective of this article is to demonstrate the application of a current concept based on the use of light for the selective removal of resins derived from orthodontic procedures. Patient has attended at the end of treatment, and the removal the orthodontic dispositive is necessary. After the removal of brackets, the composite resin remaining was removed with a fine grain and extra-fine diamond burn (FG 2135 F and FF, KG Sorensen) coupled at high speed with light emission in the specific frequency for highlight the restoration material (LED Cobra Ultra-Vision, Gnatus). The light output of this frequency showed the interface between the tooth and the orthodontic cement due to the difference in fluorescence, thus resulting in higher sensitivity of the technique and preservation of healthy dental tissue. It is concluded that the use of high-speed with light emission is an effective method for removal of resin composite remaining and it is a conservative and less invasive procedure.

Síntese e análise de compósitos experimentais para uso odontológico reforçados com nanoargila / Synthesis and analysis of experimental composites for dentistry use reinforced with nanoclay

O objetivo do presente estudo foi de avaliar os efeitos de diferentes frações de partículas de nanoargila modificadas do tipo montmorilonita Cloisite® 20A em propriedades físicas, mecânicas e biológicas de resinas experimentais do tipo nanohíbrida. Compósitos dentais foram preparados através da mistura de 30% de matriz resinosa (BisGMA/TEGDMA) em 70% de partículas de carga (vidro de bário silicato silanizado ­VB, dióxido de silício ­ SD, partículas de nanoargila MMT). Quatro grupos de compósitos experimentais foram formados, variando o percentual de nanoargila empregada (0%, 5%, 7,5%, 10%). O processamento foi realizado em uma máquina de dupla mistura (SpeedMixer DAC, Germany, 3500 rpm). A citotoxicidade in vitro do material foi avaliada baseada nas normas ISO 10993- 5-2009 e comparado com compósito comercial. Ensaios mecânicos para cálculo de Resistência à Flexão e Módulo de Elasticidade foram realizados em máquina de ensaios universal EMIC. O aparelho Acuvol® foi utilizado para o ensaio de contração de polimerização. A sorção e solubilidade dos compósitos foram calculadas baseadas nas normas ISO 4049. Os dados foram analisados estatisticamente, utilizando-se a tabela ANOVA e o Teste de Tukey para comparação dos grupos de dois em dois. O nível de significância utilizado foi de 95% (p< 0,05). Por meio do exame dos resultados, concluiu-se que foi possível esfoliar 5 e 7,5% de partículas de MMT satisfatoriamente na matriz BisGMA/TEGDMA, porém, o inserção de 10% de MMT na matriz orgânica não trouxe vantagens ao compósito, certamente por não permitir a total exfoliação de suas partículas. A inserção de 5 e 7,5% de nanoargila ao compósito dental experimental possibilitou uma diminuição da contração de polimerização do material em 22,13 e 17,4%, respectivamente. Além disso, esses dois grupos permaneceram com suas propriedades mecânicas e de absorção e solubilidade satisfatórias, além de apresentar ausência de citotoxicidade para as células fibroblasticas L929 testadas

The aim of the present study was to evaluate the effect of different weight fractions of modified montmorillonite nanoclay fillers Cloisite ® 20A on mechanical, physical and biological properties of nanohybrid experimental resins. Dental composites were prepared by mixing 30% of resin matrix (BisGMA / TEGDMA) to 70% of particulate fillers (Silanized barium silicate particles - BS, silicone dioxide - SD, montmorillonite nanoclay cloisite 20AMMT). Four groups of experimental composite were formed with various fractions of the nanoclay fillers (0%; 5%; 7,5%; 10% ). Processing was performed using a dual high speed mixing machine (SpeedMixer DAC, Germany, 3500 rpm). In vitro citotoxicity of the material was calculated based on standards ISO 10993-5-2009 and compared to a comercial composite. Tensile strenght and elastic modulus were performed using an universal test machine EMIC. The volumetric shrinkage was calculated by Acuvol® machine. Water sorption and solubility were measured based on International Standard ISO 4049. Data were statistically analyzed by ANOVA and Tukey Test for multiple comparisons. The significance level utilized was 95% (p < 0,05). By the results, it was concluded that it is possible to exfoliate nicely 5 and 7.5% of MMT particles inside Bis-GMA/TEGDMA matrix. However, insertion of 10% of MMT did not improve composite, certainly, because the total exfoliation of particles did not occured. Insertion of 5 and 7.5% of nanoclay in dental composite diminished polymerization shrinkage in 22,13% and 17,4% , respectively. Furthermore, these two groups maintained their mechanical properties, satisfactory sorption and solubility and also presented no citotoxicity for L929 fibroblastic cells

Evaluation of shear bond strength of different treatments of ceramic bracket surfaces / Avaliação da resistência ao cisalhamento de diferentes tratamentos na superfície de braquetes cerâmicos

OBJECTIVE: To evaluate the bonding strength of the ceramic bracket and composite resin restoration interface, using four types of treatment on the base of the bracket. METHODOLOGY: 48 photoactivated composite resin discs were used (FiltekTM Z250) contained in specimens and divided into 4 groups of 12 specimens for each group according to the type of treatment performed on the base of the brackets. Once the brackets were bonded, the specimens were subjected to shear stress carried out in a universal testing machine (MTS: 810 Material Test System) calibrated with a fixed speed of 0.5 mm / minute. The values obtained were recorded and compared by means of appropriate statistical tests - analysis of variance and then Tukey's test. RESULTS AND CONCLUSIONS: The surfaces of ceramic brackets conditioned with 10% hydrofluoric acid for 1 minute, followed by aluminum oxide blasting, 50µ, after silane application and primer application, was considered the best method to prepare surfaces of ceramic brackets prior to orthodontic esthetic bonding.

OBJETIVO: avaliar a resistência à união da interface entre braquete cerâmico e restauração de resina composta, empregando quatro tipos de tratamento na base do braquete. MÉTODOS: foram utilizados 48 discos de resina fotoativada (Filtek® Z250) incluídos em corpos de prova, divididos em quatro grupos, com 12 espécimes em cada grupo, de acordo com o tipo de tratamento realizado na base do braquete. Uma vez colados os braquetes, os corpos de prova foram submetidos à tensão de cisalhamento, realizado numa máquina universal de ensaios (MTS: 810 Material Test System) calibrada com velocidade fixa de 0,5mm/min. Os valores obtidos foram registrados e comparados por meio de médias, utilizando-se testes estatísticos adequados (análise de Variância e, posteriormente, teste de Tukey). RESULTADOS E CONCLUSÕES: o condicionamento das superfícies dos braquetes cerâmicos com ácido hidrofluorídrico a 10% por 1 minuto, seguido do jateamento com óxido de alumínio com 50um de tamanho, e posterior aplicação do silano e, depois, aplicação de adesivo, foi considerado o melhor método para o preparo de superfícies de braquetes cerâmicos previamente à colagem estética ortodôntica.

Efecto de la unidad de luz y de la profundidad de polimerización sobre la microdureza de un composite / Effect of light unit and depth on curing a composite microhardness

El objetivo de este estudio fue evaluar a través de test de microdureza el efecto de la profundidad de polimerización de un composite utilizando diferentes unidades de luz. Fueron preparados cuerpos de prueba utilizando un composite microhíbrido - Filtek Z250 (3M) en matrices de teflón con dos profundidades diferentes: 2 mm y 3 mm, conteniendo un orificio central de 2 mm de diámetro. Los valores de dureza fueron medidos en la región de superficie y en la de fondo. Fueron utilizadas tres unidades de luz, dos a base de Luz Emitida por Diodo - LED: Optilight CL (Gnatus) y Radii (SDI) y una a base de luz halógena: Ultralux (Dabialtante). Después de la fotoactivación durante 40 segundos, los cuerpos de prueba fueron almacenados en recipiente oscuro, durante 24 horas. El test de dureza Vickers fue realizado con el equipo de dureza Shimadzu Micro Hardness Testers, utilizando una carga de 300 gramos por 15 segundos. Fueron realizadas tres identaciones en cada región (superficie y fondo) de los cuerpos de prueba. Los valores de dureza fueron sometidos a análisis de variancia (ANOVA) y al test de Tukey-Kramer (p<0,05).No fue observada diferencia estadísticamente significativa entre los equipos fotoactivadores, sin embargo, el equipo Ultralux proporcionó mayores valores de dureza al composite de que los otros equipos. Considerando el tipo de equipo evaluados, no hubo diferencia estadísticamente significativa en relación a la microdureza del composite en las profundidades de 2mm e 3mm en ninguna de las regiones. Comparando las regiones de los cuerpos de prueba analizadas, (superficial y fondo), fue observada diferencia estadísticamente significativa en ambas profundidades y con todos los equipos, siendo los valores dureza Vickers mayores en la región de fondo de los cuerpos de prueba. Concluyese que entre los equipos utilizados, el Ultralux proporcionó mayor dureza al composite siendo estadísticamente significativa, sin embargo, no hubo diferencia significativa...

The aim of this study was to evaluate the influence of different depths of cure on the microhardness of a composite resin when using three different types of light units. Test specimens with a 2-mm diameter centered orifice were prepared with a microhybrid composite - Filtek Z250 (3M) using teflon matrices with two different depths: 2 mm and 3 mm. Hardness values were assessed both in superficial and deep areas. Three light units were compared: two light-emitting diode units - Optilight CL (Gnatus) and Radii (SDI), and one halogen-based light unit - Ultralux (Dabialtante). After light curing for 40 minutes, the specimens were stored in a lightproof container for 24 hours. The Vickers hardness test was carried out by the Shimadzu Micro Hardness Tester at a load f 300 grams for 15 seconds. Three test indentations were made in each area (superficial and deep) of the specimens. Mean values of hardness were compared by the analysis of variance (ANOVA), and by the Tukey-Kramer test at 5%. They demonstrated a statistically significant difference between the three light units. The Ultralux device yielded the highest values of hardness regardless the depth of the specimens. It was also observed no statistically significant difference in terms of hardness when comparing the two thicknesses of composite resin within each studied group.

Square-wave voltammetric determination of rutin in pharmaceutical formulations using a carbon composite electrode modified with copper (II) phosphate immobilized in polyester resin

A carbon composite electrode modified with copper (II) phosphate immobilized in a polyester resin (Cu3(PO4)2-Poly) for the determination of rutin in pharmaceutical samples by square-wave voltammetry is described herein. The modified electrode allows the determination of rutin at a potential (0.20 V vs. Ag/AgCl (3.0 mol L-1 KCl)) lower than that observed at an unmodified electrode. The peak current was found to be linear to the rutin concentration in the range from 9.9 × 10-8 to 2.5 × 10-6 mol L-1, with a detection limit of 1.2×10-8 mol L-1. The response of the electrode was stable, with no variation in baseline levels within several hours of continuous operation. The surface morphology of the modified electrode was characterized by scanning electron microscopy (SEM) and energy dispersive X-ray (EDX) system. The results obtained are precise and accurate. In addition, these results are in agreement with those obtained by the chromatographic method at a 95% confidence level.

Descreve-se um eletrodo de carbono modificado com fosfato de cobre (II) imobilizado em uma resina de poliéster (Cu3(PO4)2-Poly) para a determinação de rutina em amostras farmacêuticas por voltametria de onda quadrada. O eletrodo modificado permite a determinação de rutina em potencial (0.20 V vs Ag / AgCl (3,0 mol L-1 KCl)) menor que o observado em um eletrodo não modificado. Verificou-se que a corrente de pico foi linear com a concentração de rutina na faixa de 9,9 × 10-8 a 2,5 × 10-6 mol L-1, com um limite de detecção de 1,2 × 10-8 mol L¹. A resposta do eletrodo foi estável, sem variação significativa dentro de várias horas de operação contínua. A morfologia da superfície do eletrodo modificado foi caracterizada por microscopia eletrônica de varredura (MEV) e pelo sistema de energia dispersiva de raios-X (EDX). Os resultados obtidos foram precisos e exatos. Ademais, estes resultados estão de acordo com aqueles obtidos pelo método cromatográfico a um nível de confiança de 95%.

Distribuição de tensões em próteses parciais fixas posteriores livres de metal com retentores intracoronários: análise em elementos finitos / Stress distribution in metal-free posterior inlay-retained fixed partial dentures: finite element analysis

Para reabilitar a ausência de um elemento dentário posterior, as próteses parciais fixas (PPF) com retentores intracoronários são uma alternativa aos implantes osseointegrados. O objetivo deste estudo foi avaliar a distribuição de tensões nessas próteses com três combinações de materiais: cerâmica de zircônia parcialmente estabilizada por ítria (ZPEI) revestida por cerâmica de fluorapatita (α), cerâmica de dissilicato de lítio (β) ou compósito fibrorreforçado (γ). Na composição α, foram analisadas a presença ou ausência da cerâmica de revestimento na parede cervical das caixas proximais e três variações na área total da seção transversal dos conectores (4 mm de largura x 3,2, 4,2 ou 5,2 mm de altura). Em 8 modelos bidimensionais de elementos finitos, uma carga vertical de 500 N foi aplicada na fossa central do pôntico e as tensões principais máximas (tração) e mínimas (compressão) foram apontadas em MPa. Inicialmente foram avaliados os 6 modelos com PPF de ZPEI e suas variações. Os maiores valores das tensões de tração foram encontrados no terço cervical dos conectores. Quando presente nestas regiões, a cerâmica de revestimento recebeu tensões acima do limite de sua resistência à flexão. Na comparação entre os modelos sem cerâmica de revestimento na parede cervical das caixas proximais, mesmo aquele com conectores de 3,2 x 4 mm, cuja infraestrutura apresentava 2,5 x 3 mm, poderia ser recomendado para uso clínico. Altos valores de tensões de compressão foram registrados entre o terço oclusal e médio dos conectores, correspondente à união entre as cerâmicas, o que poderia ocasionar, devido à flexão, falhas adesivas. Posteriormente, o modelo de ZPEI com a cerâmica de fluorapatita ausente da parede cervical das caixas proximais e área total dos conectores de 4,2 x 4 mm foi comparado aos dois outros materiais com conectores de mesma área. Na PPF de dissilicato de lítio, os valores representaram uma provável violação do limite de sua resistência à flexão...

Inlay-retained fixed partial dentures (IRFPD) are an alternative to osseointegrated implants to replace a single missing posterior tooth. The aim of this study was to evaluate the stress distribution within these prostheses with three material combinations: yttria-tetragonal zirconia polycrystal (Y-TZP) ceramic veneered with fluorapatite ceramic (α), lithium-disilicate ceramic (β) or fiber-reinforced composite (γ). In composition α, an analysis was conducted on the presence or absence of the veneering ceramic on the cervical wall of the proximal boxes and three variations in the total area of the connectors’ cross-section (4 mm in width x 3.2, 4.2 or 5.2 mm in height). In 8 two-dimensional finite element models, a vertical load of 500 N was applied on the central fossa of the pontic. Maximum (tension) and minimum (compression) principal stresses were then shown in MPa. First, the 6 models with Y-TZP fixed partial dentures (FPD) and their variations were evaluated. The highest values of tensile stresses were found at the cervical third of the connectors. When present in these regions, the veneering ceramic received stresses beyond its flexural strength limit. In the comparison among models without veneering ceramic on the cervical wall of the proximal boxes, even the model with connectors of 3.2 x 4 mm, whose framework presented 2.5 x 3 mm, could be recommended for clinical use. High values of compressive stresses were recorded between the middle and occlusal thirds of the connectors, corresponding to the juncture of the ceramics. Owing to flexure, these stresses might lead to adhesive failures. Then, the Y-TZP model without fluorapatite ceramic on the cervical wall of the proximal boxes and total connector area of 4.2 x 4 mm was compared to the other two materials with connectors of the same area. For the lithium-disilicate FPD, the observed values would probably exceed its flexural strength limit...

Efeito do Bisel no Esmalte Sobre a Microinfiltração em Preparos Classe I em Molares Decíduos / Effect of Enamel Bevel on Microleakage in Class I Cavities in Primary Molars

Objetivo: Avaliar in vitro a influência da terminação marginal do preparo cavitário Classe I sobre a qualidade adesiva em restaurações compósitas realizadas em primeiros e segundos molares decíduos.Método: Dois preparos cavitários foram realizados na oclusal de vinte molares decíduos hígidos, sendo 20 preparos em primeiros molares e 20 em segundos molares, totalizando quarenta preparos cavitários. Após escolha aleatória, 20 preparos não receberam o bisel reto (grupo controle, GI, n=20) enquanto os demais preparos, grupo experimental, (GII, n=20) receberam um bisel reto com 0,5 mm de extensão no ângulo cavo û superficial feito com ponta diamantada ultra-fina 2200 FF. Para o procedimento restaurador, utilizou-se condicionamento ácido total com ácido fosfórico a 37% por 30s, sistema adesivo Prime & Bond NT® e compósito TPH® Spectrum cor A2. Para avaliação da qualidade adesiva, os dentes foram isolados com verniz, exceto às restaurações e 1,0 mm além das suas margens, e permaneceram em contato direto com uma solução aquosa de nitrato de prata a 50%, por 24 h. Em seguida, estes dentes foram clivados mesiodistalmente, e as restaurações avaliadas com 40 vezes de aumento. Dois avaliadores calibrados classificaram independentemente as restaurações de acordo com escores que variaram de zero (ausência de microinfiltração) a três (máxima microinfiltração). Os dados foram analisados descritivamente e tratados com os testes de Wilcoxon, Qui-quadrado e exato de Fisher a um nível de confiança de 95%.Resultados: O GII mostrou maiores escores de microinfiltração que o GI (p<0.001; p=0.0001). Os primeiros molares decíduos sofreram mais microinfiltração na presença de bisel (p=0.0003). Conclusão: O bisel no ângulo cavo-superficial em preparos Classe I aumentou a infiltração marginal nas restaurações compósitas em molares decíduos, principalmente nos primeiros molares

Objective: To evaluate in vitro the influence of Class I cavity marginal preparation on the adhesive quality in composite resin restorations placed in first and second primary molars.Method: Two cavities were prepared on the oclusal face of twenty sound primary molars, being twenty cavities in first molars and twenty in second molars, totalizing forty cavities. After random allocation, twenty cavities did not receive a straight bevel (control group, GI, n=20) while in the other cavities (experimental group, GII, n=20) a 0.5 mm straight bevel was made in the cavosurface angle with ultra-fine diamond bur 2200 FF. The restorative procedure included 37% phosphoric acid etching for 30 s, application of Prime & Bond NT®adhesive system and placement of TPH®Spectrum composite resin (shade A2). For evaluation of the adhesive quality, the teeth were coated with varnish, except for the restorations and a 1.0-mm-wide window beyond its margins, and were immersed in a 50% silver nitrate aqueous solution for 24 h. Next, the teeth were cleaved mesiodistally and the restorations were examined at ×40 magnification. Two independent calibrated examiners classified the restorations according to scores from zero (absence of microleakage) to three (maximum microleakage). Data were analyzed descriptively and treated with Wilcoxon, Chi-Square and FisherÆs exact tests at a confidence level of 95%.Results: GII presented higher microleakage scores than GI (p<0.001; p=0.0001). The primary first molars showed greater microleakage in the presence of bevel (p=0.0003). Conclusion: Beveling the cavosurface angle in Class I cavities increased marginal microleakage in the composite resin restorations placed in primary molars, especially in the first molars

Distribuição de tensões em próteses parciais fixas posteriores livres de metal com retentores intracoronários: análise em elementos finitos / Stress distribution in metal-free posterior inlay-retained fixed partial dentures: finite element analysis

Para reabilitar a ausência de um elemento dentário posterior, as próteses parciais fixas (PPF) com retentores intracoronários são uma alternativa aos implantes osseointegrados. O objetivo deste estudo foi avaliar a distribuição de tensões nessas próteses com três combinações de materiais: cerâmica de zircônia parcialmente estabilizada por ítria (ZPEI) revestida por cerâmica de fluorapatita (α), cerâmica de dissilicato de lítio (β) ou compósito fibrorreforçado (γ). Na composição α, foram analisadas a presença ou ausência da cerâmica de revestimento na parede cervical das caixas proximais e três variações na área total da seção transversal dos conectores (4 mm de largura x 3,2, 4,2 ou 5,2 mm de altura). Em 8 modelos bidimensionais de elementos finitos, uma carga vertical de 500 N foi aplicada na fossa central do pôntico e as tensões principais máximas (tração) e mínimas (compressão) foram apontadas em MPa. Inicialmente foram avaliados os 6 modelos com PPF de ZPEI e suas variações. Os maiores valores das tensões de tração foram encontrados no terço cervical dos conectores. Quando presente nestas regiões, a cerâmica de revestimento recebeu tensões acima do limite de sua resistência à flexão. Na comparação entre os modelos sem cerâmica de revestimento na parede cervical das caixas proximais, mesmo aquele com conectores de 3,2 x 4 mm, cuja infraestrutura apresentava 2,5 x 3 mm, poderia ser recomendado para uso clínico. Altos valores de tensões de compressão foram registrados entre o terço oclusal e médio dos conectores, correspondente à união entre as cerâmicas, o que poderia ocasionar, devido à flexão, falhas adesivas. Posteriormente, o modelo de ZPEI com a cerâmica de fluorapatita ausente da parede cervical das caixas proximais e área total dos conectores de 4,2 x 4 mm foi comparado aos dois outros materiais com conectores de mesma área. Na PPF de dissilicato de lítio, os valores representaram uma provável violação do limite de sua resistência à flexão...

Inlay-retained fixed partial dentures (IRFPD) are an alternative to osseointegrated implants to replace a single missing posterior tooth. The aim of this study was to evaluate the stress distribution within these prostheses with three material combinations: yttria-tetragonal zirconia polycrystal (Y-TZP) ceramic veneered with fluorapatite ceramic (α), lithium-disilicate ceramic (β) or fiber-reinforced composite (γ). In composition α, an analysis was conducted on the presence or absence of the veneering ceramic on the cervical wall of the proximal boxes and three variations in the total area of the connectors’ cross-section (4 mm in width x 3.2, 4.2 or 5.2 mm in height). In 8 two-dimensional finite element models, a vertical load of 500 N was applied on the central fossa of the pontic. Maximum (tension) and minimum (compression) principal stresses were then shown in MPa. First, the 6 models with Y-TZP fixed partial dentures (FPD) and their variations were evaluated. The highest values of tensile stresses were found at the cervical third of the connectors. When present in these regions, the veneering ceramic received stresses beyond its flexural strength limit. In the comparison among models without veneering ceramic on the cervical wall of the proximal boxes, even the model with connectors of 3.2 x 4 mm, whose framework presented 2.5 x 3 mm, could be recommended for clinical use. High values of compressive stresses were recorded between the middle and occlusal thirds of the connectors, corresponding to the juncture of the ceramics. Owing to flexure, these stresses might lead to adhesive failures. Then, the Y-TZP model without fluorapatite ceramic on the cervical wall of the proximal boxes and total connector area of 4.2 x 4 mm was compared to the other two materials with connectors of the same area. For the lithium-disilicate FPD, the observed values would probably exceed its flexural strength limit...

A busca da estética em casos de discrepância ósseo-dentária / In searching of esthetic in case of tooth-size discrepancy

Em Odontologia, o desafio não é apenas produzir boa oclusão, mas obter boa oclusão com bom resultado estético. E a escolha da solução mais adequada depende das características específicas de cada caso e da interação com as especialidades afins devem ser consideradas na elaboração e execução do plano de tratamento. A ausência de proporcionalidade dimensional entre os dentes maxilares e mandibulares impossibilita a intercuspidação, overjet e overbite adequados, além de um bom resultado estético. Nos casos de discrepância ósseodentária estão indicados stripping ou acréscimo e abertura ou fechamento de espaço na arcada oposta. Nesses casos, as dificuldades envolvidas devem ser ponderadas. No caso clínico apresentado os recursos biomecânicos da Ortodontia e os benefícios da Dentística foram aplicados com sucesso.

In Dentistry the challenge is not to produce a good occlusion, but an aesthetic smile in a good occlusion. The choice of best solution depends on the specific characteristics of each case and the interaction with the similar specialties. The elaboration and execution of the treatment plan must be considered. The absence of dimensional proportionality between mandibular and maxillary teeth disables the intercuspation, overjet and overbite adjusted with a good aesthetic result. In cases of tooth-size discrepancy stripping or addition and opening or closing of space in opposite arch are indicated. In these cases, the involved difficulties and specific needs must be considered altogether. In the clinical case presented orthodontic biomechanic resources and the benefits of the Cosmetic Dentistry had been applied successfully.

Osseointegração clínica-radiológica do compósito hidroxiapatita-lignina entre implante metálico e tecido ósseo em coelho / Clinical-radiographic osseointegration of hydroxyapatite-lignin composite between metallic implant and bone tissue in rabbit

Para avaliar o compósito hidroxiapatita-lignina na osseointegração entre implante metálico e o tecido ósseo, foram utilizados 20 coelhos adultos, nos quais foi realizada uma falha óssea na face lateral proximal de ambas as tíbias. Na tíbia esquerda, introduziu-se, no canal medular, um pino intramedular de Schanz revestido com o compósito em sua parte rosqueada, após o preenchimento daquele com 1000mg do compósito. A falha cortical foi preenchida com o compósito. O mesmo foi feito na tíbia direita, porém sem a utilização do compósito, servindo como controle. A avaliação clínica baseou-se na deiscência, claudicação, sensibilidade dolorosa e circunferência tibial. Foram realizadas radiografias imediatamente após a cirurgia e aos oito, 30, 60, 90 e 120 dias do pós-operatório. A maioria dos animais apresentou evolução clínica normal. Nas radiografias do grupo tratado, houve decréscimo da radiopacidade no defeito e no espaço medular até tornar-se semelhante à do osso circunvizinho, quadro inverso ao do grupo-controle. Conclui-se que o compósito hidroxiapatita-lignina não mostrou indícios clínicos de rejeição e que o tecido visualizado na altura da falha óssea e ao redor do pino intramedular tinha radiopacidade semelhante à do osso circunvizinho, o que sugere que o material promoveu a integração com o tecido ósseo.

This study evaluated a sinthetic hydroxyapatite-lignin composite for osseoingration between metallic implant and bone tissue. Twenty New Zealand rabbits were used. A defect was made a the proximal region of lateral surfaces of both tibias. An intramedullary pin was inserted in the medullary cavity of the left tibia after filling the cavity with 1,000mg of the composite and covering the thread part of the pin with the composite. The same procedure was made in control tibias without the composite. Clinical evaluation was based on inflammatory reaction, dehiscence, lameness, pain, and tibial circumference. Radiographs were made immediately after surgery and then on days eight, 30, 60, 90, and 120. Most of the animals presented normal clinical progression. Radiographies of treated group showed decrease in the defect and medullary cavity radiopacity to the same pattern of the surrounding bone, while the contrary happened in control group; but, in this group, the medullary cavity remained radioluscent at the last observation date. It can be concluded that the hydroxyapatite-lignin composite did not show clinical signs of rejection and that radiopacity of the tissue in the bone defect and surrounding the pin was similar to bone radiopacity, suggesting that the material promoted osseointegration.

Resposta tecidual ao compósito 50 por cento hidroxiapatita: 50 por cento poli-hidroxibutirato para substituição óssea em coelhos / Tissue response to the composite 50 percent hydroxyapatite: 50 percent polyhydroxybutyrate for bone substitution in rabbits

Avaliaram-se a biocompatibilidade, a osseointegração, a osseocondução e a biodegradação de compósitos de 50 por cento hidroxiapatita (HAP-91®) e 50 por cento poli-hidroxibutirato. O compósito foi implantado em defeitos ósseos em 12 coelhos (grupo experimental), sendo comparado a defeitos não preenchidos (grupo-controle, de igual número). Os parâmetros clínicos dor, claudicação, infecção, deiscência e edema foram avaliados nos primeiros oito dias após a cirurgia e aos 45 e 90 dias. Radiografias foram realizadas aos oito, 45 e 90 dias após a cirurgia em quatro animais por grupo que, em seguida, foram submetidos à eutanásia para coleta de amostras destinadas a análises histológica e histomorfométrica. Não ocorreram diferenças entre os grupos para todos os parâmetros clínicos. Radiografias demonstraram um compósito com radiopacidade semelhante à do osso vizinho e contato direto entre osso e compósito aos 45 e 90 dias. Diferença significativa foi observada entre a porcentagem dos tecidos ósseo e conjuntivo dentro do defeito nos dias oito, 45 e 90, assim como na interface aos 45 e 90 dias. Foram observadas projeções dos tecidos ósseo e conjuntivo no interior do compósito e sinais de biodegradação na ausência de infiltrado inflamatório. Pode-se concluir que o compósito é biocompatível, osseocondutor, biodegradável e se integra ao tecido ósseo.

The biocompatibility, osseointegration, osseoconductivity, and biodegradation of a 50-50 percent hydroxyapatite (HAP-91®)-polyhydroxybutyrate were evaluated. The composite was implanted in bone defects of 12 rabbits (experimental group), being compared to unfilled defects (control group, 12 animals). The clinical parameters of pain, lameness, infection, dehiscence, and edema were evaluated during the first eight days and on the 45th and 90th days after surgery. Radiographs were taken in four animals per group at 8, 45, and 90 days after surgery, when animals were euthanized to collect samples for histology and histomorphometry. Significant differences between groups for all clinical parameters were not observed. Radiographs showed a similar radiopacity of the composite and bone and their direct contact. More bone than connective tissue was found within the defect at 8, 45, and 90 days and at the interface on the 45th and 90th days. Projections of bone and connective tissue were seen inside the composite. Biodegradation signs became evident, with absence of inflammatory infiltrate. Data support that such composite is biocompatible, osseoconductive, biodegradable, and integrate to bone.

Avaliação in vitro da resistência ao cisalhamento e liberação de flúor de dois cimentos de ionômero de vidro reforçado por resina / In vitro evaluation of shear bond strength and fluoride release from two resin-reinforced glass ionomer cements

O objetivo deste estudo foi avaliar os cimentos de ionômero de vidro reforçados com resina Fuji Ortho LC e Fuji Ortho Band (GC América Corporation, Tokyo, Japan) quanto a resistência ao cisalhamento e liberação de flúor. Para avaliação da resistência ao cisalhamento utilizou-se 60 incisivos inferiores permanentes bovinos divididos em três grupos (n = 15). No Grupo 1, 2 e 3, as colagens foram realizadas com Transbond XT, Fuji Ortho LC e Fuji Ortho Band respectivamente. Após a colagem realizou-se o ensaio de cisalhamento de toda amostra à velocidade de 0,5 mm por minuto. A liberação de flúor dos materiais foram medidas durante 28 dias (1h, 24 h, 3, 7, 14, 21 e 28 dias) através de eletrodo íon seletivo conectado a um analisador de íons. Os resultados demonstraram que quanto a resistência ao cisalhamento (MPa) houve diferenças estatísticas entre os grupos 1 e 3, 2 e 3 (p > 0,05). Quanto a liberação de flúor os resultados evidenciaram diferença estatisticamente significante entre os grupos 1 e 3 e 2 e 3 em todos os tempos (p = 0.00) e entre os grupos 1 e 2 na avaliação de 3 dias de liberação de flúor (p = 0.00). Baseado nos resultados obtidos conclui-se que os materiais Transbond XT e Fuji Ortho possuem melhor resistência ao cisalhamento por??m menor liberação de flúor quando comparado ao Fuji Ortho Band.

The objective of this study was to evaluate two resin-reinforced glass ionomer cements, Fuji Ortho LC and Fuji Ortho Band (GC América Corporation, Tokyo, Japan) in terms of shear bond strength and fluoride release. Sixty bovine permanent lower incisors were divided into three groups (n = 15). In Groups 1, 2, and 3 the bonding procedures were performed with Transbond XT, Fuji Ortho LC, and Fuji Ortho Band materials respectively. Next, the samples were submitted to bond strength testing at crosshead speed of 0.5 mm/minute. Fluoride release from such materials was measured during 28 days (1h, 24 h, 3, 7, 14, 21, and 28 days) by means of selective ion electrodes connected to an ion analyser. With respect to the shear bond strength (MPa), the results demonstrated statistical differences between groups 1 and 3 as well as between groups 2 and 3. With respect to the fluoride release, the results showed statistically significant results between groups 1 and 3 as well as between groups 2 and 3 for all time periods (p = 0.00). Also, the 3-day evaluation showed statistical differences between groups 1 and 2 regarding fluoride release (p = 0.00). Based on the results obtained in the present study, one can conclude that Transbond XT and Fuji Ortho materials have a better shear bond strength than the Fuji Ortho Band one, although the latter releases less fluoride.

Influência do método de polimerização na microdureza de compósitos microhíbridos armazenados em água destilada / Influence of curing method on the micro hardness of microhybrid composites immersed in distilled water

O objetivo do presente estudo é comparar e avaliar a microdureza Vickers de um compósito restaurador microhíbrido ativado por dois tipos de unidades polimerizadoras e armazenados em água destilada. Trinta espécimes foram feitos com resina Charisma B1, para cada um dos regimes de polimerização: fotopolimerização por luz halógena, fotopolimerização por LED e fotopolimerização mais ciclo adicional em autoclave. Foram feitas duas leituras de microdureza Vickers por corpo de prova em 1 dia, 7 dias e 14 dias de imersões. O ciclo adicional de polimerização mostrou uma tendência de aumentar os valores de microdureza dos compósitos restauradores, não mostrando diferenças estatisticamente significantes entre LED e Luz Halógena (p > 0,05).

The purpose of this study is to evaluate and compare the Vickers microhardness of one microhybrid composite polymerized with different sources and stored in distilled water for up to 14 days. Thirty samples have been prepared with Charisma composite, shade B1, for each polymerization method: halogen light photopolymerization, LED photopolymerization, photopolymerization plus post-cured cycles in autoclave. Two readings of Vichers micro hardness have been done in each sample on 24h, 7days and 14 days of storage. The post curing method tended to improve the microhardness, but it was not statistically different from halogen or LED curing methods (p > 0.05). After 7 days, the hardness values were higher than the first day, but statistically not different to 14 days (p < 0.05). Post-cured samples in autoclave had an improved mean value, however, without differing from those of the LED and halogen.

Estudo comparativo da resistência à flexão da cerâmica IPS Empress 2, dos compósitos Vectris e Z-100 e das ligas metálicas Durabond e Litecast B / Flexural strength of IPS Empress 2, Vectris, Z-100 and Durabond and Litecast B metal alloys: a comparative study

A resistência comparativa à flexão dos materiais Vectris, IPS Empress 2, liga de Ni-Cr-Be-Mo (Litecast B), liga de Ni-Cr (Durabond), e resina composta Z-100, foi avaliada por meio de um ensaio mecênico de três pontos. Foram confeccionados 47 corpos-de-prova na forma de barra 25 x 5 x 2 mm, através do preenchimento de uma matriz metálica. O ensaio de flexão foi realizado numa máquina de ensaios mecânicos, MST 810 seguindo-se as normas da ISO 6872, sendo uma carga aplicada no centro dos corpos-de-prova à ua velocidade de 0,5 mm/min, registrando o valor de resistência no momento de ruptura. As médias dos valores encontrados para o Litecast B, Durabond, Vectris, IPS Empress 2 e resina composta Z-100, foram respectivamente 1637,2 Mpa, 682,2 MPa, 443,6 MPa, 172,0 MPa e 100,7 Mpa. Da anállise do teste Student t ao nível de 5% de significância, concluiu-se que o Litecast B apresentou o maior valor de resistência, seguido do Durabond e Vectris. A resina composta Z-100 apresentou o valor mais baixo de resistência, seguido da cerâmica IPS Empress 2

A comparative study of the flexural strength among IPS Empress 2, Vectris and Z-100 composites and Durabond (Ni-Cr) and Litecast B (Ni-Cr-Be-Mo) metal alloys was taken through a three point bending test. 47 bar specimens were prepared using a metallic matrix of 25 x 5 x 2 mm of dimension. The flexural test was applied in an universal testing machine MTS 810 using a similar method to the ISO 6872 standard. The load was applied at a crosshead speed of 0.5 mm/min until failure. The mean values found for Litecast B, Durabond, Vectris, IPS Empress 2 and Z-100 was respectively 163.2 Mpa, 682.2 MPa, 443.6 MPa, 172.0 MPa and 100.7 MPa. The Student T analysis at a 5% level of significance, showed that Litecast B alloy had highest flexural strength followed by Durabond alloy and Vectris. The composite resin Z-100 showed the lowest value followed by IPS Empress 2 ceramic